- A. Schulman ComAlloy Hiloy® 756 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy
A. Schulman ComAlloy Hiloy® 756 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 756 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.20% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 112 MPa | 16200 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 202 MPa | 29300 psi | ASTM D790 |
| Flexural Modulus | 15.3 GPa | 2220 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.59 J/cm | 8.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 - 290 °C | 536 - 554 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 299 - 310 °C | 570 - 590 °F |
Users viewing this material also viewed the following:
- MV Labs PT268 K2PtBr6 Potassium hexabromoplatinate(IV)
- Proto3000 Objet VeroBlack FullCure870 Rigid Opaque Prototyping Polymer
- MarkeTech AN 180 Aluminum Nitride Ceramic Substrate, 99% Purity
- Garlock 706 Compressed Inorganic Fiber Gasketing, Nitrile Binder
- Michelman® Michem® Emulsion 09730 Cationic polyethylene emulsion
- Teknor Apex Telcar® TL-87-L832-B Thermoplastic Elastomer
- A. Schulman POLYBATCH™ U-7000-HS Blowing Agent Concentrate Based In HIPS
- A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene
- DuPont Performance Polymers Crastin® SO653 NC010 PBT (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved