Polyram PE322G22 PET, 22% Glass Fiber (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PE322G22 PET, 22% Glass Fiber
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
22% Glass fiber reinforced, flame retardant PET for injection molding applications.Information provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | DIN 53479 |
| Water Absorption | 0.50 % | 0.50 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23° C, 50% RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 280 °C |
13 g/10 min @Load 4.76 lb, Temperature 536 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM-D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM-D638 |
| Flexural Strength | 150 MPa | 21800 psi | ASTM D790 |
| Flexural Modulus | 6.70 GPa | 972 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 226 °C | 439 °F | DIN 53461 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
|
| Glow Wire Test | 960 °C | 1760 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- DuPont™ Surlyn® NWL Sodium Ionomer Resin for Blown and Cast Film (discontinued **)
- LG Chemical GPPS 15NF(I) PS, High Transparency, Heat Resistance
- Lanxess Pocan® B 3233 HR 000000 Polybutylene Terephthalate, 30% Glass Fibers
- Solvay Chemicals Strontium carbonate granular
- Solvay Technyl® A 216 V30 Nylon 66, 30% Glass Fiber, EH0
- Tra-Con Tra-Bond 862-7 General Purpose Epoxy Adhesive
- Dow Corning HS II BASE & 10:1 CLAY CATALYST
- Arlon R35928R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved