SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyimide, Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Extem |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermoplastic Polyimide Extem* XH1015 Resin.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Water Absorption | 0.60 % @Time 173000 sec |
0.60 % @Time 48.0 hour |
ASTM D570 |
| Water Absorption at Saturation | 2.3 % | 2.3 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.012 cm/cm @Thickness 3.20 mm |
0.010 - 0.012 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min @Load 6.60 kg, Temperature 367 °C |
10 g/10 min @Load 14.6 lb, Temperature 693 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 101 MPa | 14600 psi | 5 mm/min; ISO 527 |
| 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 7.0 % | 7.0 % | 5 mm/min; ISO 527 |
| 10 % | 10 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.10 GPa | 450 ksi | 1 mm/min; ISO 527 |
| 3.42 GPa | 496 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| 168 MPa | 24400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.87 GPa | 416 ksi | 2 mm/min; ISO 178 |
| 3.13 GPa | 454 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C @Temperature 23.0 - 150 °C |
28.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 237 °C @Thickness 6.40 mm |
459 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 247 °C | 477 °F | Rate B/120; ISO 306 |
| 250 °C | 482 °F | Rate B/50; ISO 306 | |
| 260 °C | 500 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPR-40G Black Polypropylene Homopolymer (PP Homopolymer)
- PolyOne Geon™ Vinyl Wire & Cable W3400L Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics Lexan® SLX2432T PC Copolymer
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.250" thick)
- Styron CALIBREâ„¢ 7104-8 Polycarbonate
- Master Bond Mastersil 153 Two Component, High Temperature Resistance Silicone Adhesive
- COI Ceramics Al2O3SiO2 Oxide Hollow Spheres
- DSM Novamid® 1013PL1 NAT PA6-MX
- PolyOne Synplast™ 9P-N Di Nonyl Phthalate
Copyright © lookpolymers.com All Rights Reserved