- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 92.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 92.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| PTS Trilac® ABS-EX1000 High Impact Extrusion Grade ABS Resin Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific) Lexan* JK2000 compound is a glass reinforced, non-Br and non-Cl FR polycarbonate blends designed for thinwall molding applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
| Polimeri Europa SINKRAL C433/M3 ABS, Heat Stabilized
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,EG,095-08-16-15 Special low gloss grade for extrusion and calendering, with high mattness and medium impact resist.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
| Polimeri Europa SINKRAL PD M323 ABS
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-25-16-25 General purpose injection moulding grade that exhibits outstanding flow and thermal stability duri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 - 146 °C | 198 - 295 °F | Average value: 130 °C Grade Count:47 |
| Overview of materials for Polycarbonate/ABS Alloy, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, Glass Fiber Filled". Each property range of values reported is minimum and maxi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
| Ineos ABS Lustran® 448 Key Features:UnfilledHigh impact or high impact modifiedSuitable processing methods:Injection molding |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C @Thickness 6.35 mm |
198 °F @Thickness 0.250 in |
ASTM D648 |
| IRPC Polimaxx Porene SR101 Acrylonitrile Butadiene Styrene Applications:extrusion sheetrefrigerator door liners and inner box linerspicnic coolerssnow boatsluggage cases |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY GN5001RF PC/ABS, Halogen Free Flame Retardant Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, Good FlowApplication: E&E (TV, Navigation Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER, Transparent, Low processing Temperature, High flow with excellent impact, UV stabilized. For In Mold Decoration /Labeling. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75 |
| Styrolution Terblend® S NM-31 ASA / PA Terblend® S is a UV-stabilized ASA/PA blend with high impact strength, easy flow and pronounced color fastness. It is especially suitable for unpainted highly UV-exposed automotive interior parts.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP TH0300B PU LNP* Thermocomp* Th0300B is a compound based on Polyurethane containing proprietary fillers. Characteristics of this grade are High Specific Gravity. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Unannealed; ASTM Data |
| Styron Magnum™ 9555 ABS, High Impact MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75/Af |
| Solvay TECHNYL® 2710IR PA66, DRY Description: TECHNYL® 2710 IR is an unfilled polyamide 6.6, impact modified, for injection molding. The product is available in natural color, and in colors on request.Benefits: This product, use.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75-2 |
| Borealis HA104E Polypropylene Homopolymer HA104E is a natural high molecular weight, high melt flow rate polypropylene homopolymer characterized by well-balanced stiffness to impact strength ratio at increased processing properties. Applica.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 120°C per hour; ISO 752 |
| Total PPC 7810 Polypropylene, Heterophasic Copolymer, High Impact Polypropylene PPC 7810 is a very high impact heterophasic copolymer with a Melt Flow index of 15 g/10 min.Polypropylene PPC 7810 has been specially developed for high impact and heavy duty applicati.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| TPI Porene® ABS-GA803 High Gloss, UV Resistant ABS Resin Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| TPI Porene® ABS-SR101 High Impact Extrusion Grade ABS Resin Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 120°C per hour; ISO 752 |
| Total PPC 3060 MW5 Polypropylene, Heterophasic Copolymer, Automotive Polypropylene AUTOMOTIVE PPC 3060 MW5 is a heterophasic copolymer with a Melt Flow index of 7 g/10 min.Polypropylene AUTOMOTIVE PPC 3060 MW5 is a high impact copolymer with heat stabilization packag.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 120°C per hour; ISO 75-2 |
| Total PPC 3640 Polypropylene, Heterophasic Copolymer ATOFINA Polypropylene PPC 3640 is a nucleated heterophasic copolymer. PPC 3640 is characterized by improved stiffness, creep resistance and high impact resistance.ApplicationPPC 3640 has been devel.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 120°C per hour; ISO 75-2 |
| Total PPC 3645 Polypropylene, Heterophasic Copolymer ATOFINA Polypropylene PPC 3645 is a nucleated heterophasic copolymer. PPC 3645 is characterized by improved stiffness, creep resistance and high impact resistance.ApplicationPPC 3645 has been devel.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 120°C per hour; ISO 75-2 |
| Total PPC 4663 Polypropylene, Heterophasic Copolymer ATOFINA Polypropylene PPC 4663 is heterophasic copolymer. PPC 4663 is characterized by a combination of ease of processing and good manufacturing article properties in applications ranging from hou.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Eastman Tenite 360A4861307 Cellulose Acetate Propionate, Clear, Trsp Applications:Blood TherapyDrug DeliveryIV ComponentsMedical DevicesSurgical InstrumentsKey Attributes:Chemical resistance to most medical solvents including lipids and IPAEase of processingGamma and.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75-1/-2 |
| Covestro Bayblend® FR 3000 Polycarbonate + ABS, Flame Retardant Grade Injection molding gradeeasy-flow gradeVicat/B 120 temperature = 97 °CUL-listing 94 V-0 (1.5 mm) antimony-, chlorine- and bromine-free flame retardantglow wire test (GWFI): 960 °C (2.0 mm)no j.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75-1,-2 |
| Covestro Bayblend® FR3000 PC/ABS Blend Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Easy-.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Unannealed; ASTM Data |
| Dow Retain® ABS 7490 ABS Data provided by Dow Chemical. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Annealed; ASTM Data |
| Dow Prevail® 3100 ABS + Polyurethane PREVAIL® 3100 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Ashley Polymers Ashlene® ABS 220 High impact for extrusion. Applications: Extrusion sheet applications including refrigerator door liners and inner box liners, picnic coolers, snow boats, luggage cases, etc.Data provided by the m.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Ashley Polymers Ashlene® ABS Resin F-221 High gloss, high impact, extrusion grade.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Washington Penn PPC7UF0-Black Polypropylene, High Flow Copolymer Injection Molding Grade. Heat Stabilized. Meets Ford ESH-M4D293-B Spec.Data provided by Washington Penn Plastic Co., Inc. |
|||