TPI Porene® ABS-SR101 High Impact Extrusion Grade ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Thai Petrochemical Industry Co. LTD. |
| Trade Name | Porene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TPI Porene® ABS-SR101 High Impact Extrusion Grade ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 43.0 MPa @Thickness 3.17 mm |
6240 psi @Thickness 0.125 in |
|
| Flexural Yield Strength | 59.1 MPa @Thickness 3.17 mm |
8570 psi @Thickness 0.125 in |
|
| Flexural Modulus | 1.93 GPa @Thickness 3.17 mm |
280 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 2.94 J/cm @Thickness 6.35 mm |
5.51 ft-lb/in @Thickness 0.250 in |
|
| 3.58 J/cm @Thickness 3.17 mm |
6.71 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HP2R PC
- DuPont Performance Polymers Zytel® 73G35HSL BK262 Nylon 6 (Unverified Data**)
- Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes
- Master Bond EP112M Two Component, Medium Viscosity Heat Curing Cycloaliphatic Epoxy Resin
- Dow Corning SYL-OFF® SL 400 COATING
- CP-Polymer-Technik Wellamid® 6600 GV 35 HWCP 35% Glass Fiber Nylon 66, Heat Stabilized, Conditioned
- ExxonMobil SAE 40 Mobilgard M50
- Ascend Performance Materials Vydyne® 47H BK0501 Nylon 66, Impact Modified, DAM
- Pyrotek ISOCAST Insulating Refractory Castable
Copyright © lookpolymers.com All Rights Reserved