Borealis HA104E Polypropylene Homopolymer

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Borealis
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis HA104E Polypropylene Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HA104E is a natural high molecular weight, high melt flow rate polypropylene homopolymer characterized by well-balanced stiffness to impact strength ratio at increased processing properties. Applications HA104E is recommended for non-pressure pipes and fittings, structured wall pipes and profiles and sheets.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in³	ISO 1183
Melt Flow	0.75 g/10 min @Load 2.16 kg, Temperature 230 °C	0.75 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	35.0 MPa	5080 psi	50mm/min; ISO 527-2
Elongation at Yield	10 %	10 %	50mm/min; ISO 527-2
Tensile Modulus	1.49 GPa	216 ksi	1mm/min; ISO 527
Charpy Impact, Notched	0.450 J/cm² @Temperature 23.0 °C	2.14 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	92.0 °C	198 °F	ISO 75-2
Vicat Softening Point	94.0 °C @Load 5.10 kg	201 °F @Load 11.2 lb	ISO 306

Processing Properties	Metric	English
Middle Barrel Temperature	190 - 230 °C	374 - 446 °F
Die Temperature	200 - 230 °C	392 - 446 °F
Melt Temperature	200 - 230 °C	392 - 446 °F
Head Temperature	200 - 230 °C	392 - 446 °F