SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Lexan®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Lexan* JK2000 compound is a glass reinforced, non-Br and non-Cl FR polycarbonate blends designed for thinwall molding applications.

Physical Properties	Metric	English	Comments
Specific Gravity	1.39 g/cc	1.39 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.00050 - 0.0015 cm/cm @Thickness 3.20 mm	0.00050 - 0.0015 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0015 - 0.0035 cm/cm @Thickness 3.20 mm	0.0015 - 0.0035 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	22 g/10 min @Load 2.16 kg, Temperature 260 °C	22 g/10 min @Load 4.76 lb, Temperature 500 °F	ASTM D1238
	36 g/10 min @Load 1.20 kg, Temperature 300 °C	36 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	58.0 MPa	8410 psi	5 mm/min; ISO 527
	59.0 MPa	8560 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	59.0 MPa	8560 psi	Type I, 5 mm/min; ASTM D638
	59.0 MPa	8560 psi	5 mm/min; ISO 527
	60.0 MPa	8700 psi	SABIC - Japan Method
Elongation at Break	2.8 %	2.8 %	5 mm/min; ISO 527
	2.9 %	2.9 %	Type I, 5 mm/min; ASTM D638
	10 %	10 %	SABIC - Japan Method
Elongation at Yield	2.5 %	2.5 %	5 mm/min; ISO 527
	2.6 %	2.6 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	7.37 GPa	1070 ksi	5 mm/min; ASTM D638
	7.66 GPa	1110 ksi	1 mm/min; ISO 527
Flexural Strength	103 MPa	14900 psi	1.3 mm/min, 50 mm span; ASTM D790
	106 MPa	15400 psi	2 mm/min; ISO 178
	108 MPa	15700 psi	ASTM D790
Flexural Yield Strength	107 MPa	15500 psi	2 mm/min; ISO 178
Flexural Modulus	6.89 GPa	999 ksi	1.3 mm/min, 50 mm span; ASTM D790
	6.90 GPa	1000 ksi	ASTM D790
	7.27 GPa	1050 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.370 J/cm	0.693 ft-lb/in	ASTM D256
Izod Impact, Unnotched	3.31 J/cm	6.20 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	4.00 kJ/m²	1.90 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	23.0 kJ/m²	10.9 ft-lb/in²	80104; ISO 180/1U
Dart Drop, Total Energy	14.0 J @Temperature 23.0 °C	10.3 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	18.0 µm/m-°C @Temperature 23.0 - 80.0 °C	10.0 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-2
	28.8 µm/m-°C @Temperature -40.0 - 40.0 °C	16.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
CTE, linear, Transverse to Flow	61.2 µm/m-°C @Temperature -40.0 - 40.0 °C	34.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	76.0 µm/m-°C @Temperature 23.0 - 80.0 °C	42.2 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	92.0 °C @Thickness 3.20 mm	198 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	86.0 °C @Thickness 3.20 mm	187 °F @Thickness 0.126 in	unannealed; ASTM D648
	89.0 °C @Thickness 6.40 mm	192 °F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	93.0 °C	199 °F	Rate B/120; ISO 306
	102 °C	216 °F	Rate B/50; ASTM D1525
UL RTI, Electrical	60.0 °C	140 °F	UL 746B
UL RTI, Mechanical with Impact	60.0 °C	140 °F	UL 746B
UL RTI, Mechanical without Impact	60.0 °C	140 °F	UL 746B
Flammability, UL94	V-0 @Thickness 1.00 mm	V-0 @Thickness 0.0394 in	UL 94