SABIC Innovative Plastics LNP THERMOCOMP TH0300B PU
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP TH0300B PU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* Th0300B is a compound based on Polyurethane containing proprietary fillers. Characteristics of this grade are High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 3.02 g/cc | 3.02 g/cc | ASTM D792 |
| Density | 3.01 g/cc | 0.109 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 14.0 MPa | 2030 psi | Type I, 5 mm/min; ASTM D638 |
| 15.0 MPa | 2180 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | Type I, 5 mm/min; ASTM D638 |
| 18.0 MPa | 2610 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 31.2 % | 31.2 % | Type I, 5 mm/min; ASTM D638 |
| 31.3 % | 31.3 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 11.5 % | 11.5 % | Type I, 5 mm/min; ASTM D638 |
| 11.5 % | 11.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 1.09 GPa | 158 ksi | 1 mm/min; ISO 527 |
| 1.24 GPa | 180 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 18.0 MPa | 2610 psi | ISO 178 |
| Flexural Modulus | 0.990 GPa | 144 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.09 GPa | 158 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.58 J/cm | 2.96 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.3 J/cm | 28.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 118 kJ/m² | 56.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 22.0 J @Temperature 23.0 °C |
16.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 15.0 J | 11.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 99.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
55.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 109 µm/m-°C @Temperature -30.0 - 30.0 °C |
60.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 49.0 °C @Thickness 3.20 mm |
120 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polykemi AB POLYform POM C M90 GF30 Polyoxymethylene
- Fiberfil® J-60/20/FR Polypropylene Homopolymer, 20% Glass Reinforced, Flame Retardant
- SYNTHOS Koplen® 0513 F Expandable Polystyrene
- EMS-Grivory Grivory® BG-25 HM PA6-GF25
- DuPont Teijin Films Melinex® 329 Polyester Film, 1400 Gauge
- Radici Radilon® A ESL128 (dry) Nylon 66
- Master Bond Supreme 10HTFL One Part Epoxy Cures at 250°F
- Beijing Evergrow Resources PTFE Porous Film
Copyright © lookpolymers.com All Rights Reserved