| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 448.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features:UnfilledHigh impact or high impact modifiedSuitable processing methods:Injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.4 MPa | 6580 psi | |
| Elongation at Break | 25 % | 25 % | Nominal |
| Elongation at Yield | 3.6 % | 3.6 % | |
| Tensile Modulus | 2.31 GPa | 335 ksi | |
| Charpy Impact Unnotched | 11.0 J/cm² @Temperature -30.0 °C |
52.4 ft-lb/in² @Temperature -22.0 °F |
|
| Charpy Impact, Notched | 3.60 J/cm² | 17.1 ft-lb/in² | |
| 0.870 J/cm² @Temperature -30.0 °C |
4.14 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL Recognized |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL Recognized |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection Molding |
| Mold Temperature | 60.0 °C | 140 °F | Injection Molding |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | |
| Injection Pressure | 55.0 MPa | 7980 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1494T PC Copolymer
- Polymax® Maxelast® P1890 TPE, PP Overmold or Standalone use
- Osprey Metals 80/20 Ni Cr Powder (Grade 80% - 22)
- Kingfa JH720 G30 30% Glass Fiber Reinforced PC
- LG Chemical LUPOL GP2150 PP+GF15%
- Lord Adhesives Chemglaze® V004 Polyurethane Coating
- Saint-Gobain CHR® SG03-14(R) Premium Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- Saint-Gobain Chemfab® 3 Primary PTFE-Coated Glass
- BASF Pluracol® GP 430R Specialty Polyol
- Channel Industries 5500 Lead Zirconate Titanate Piezoelectric
Copyright © lookpolymers.com All Rights Reserved