- Acrylonitrile Butadiene Styrene (ABS), Extruded
- PTS Trilac® ABS-EX1000 High Impact Extrusion Grade ABS Resin
PTS Trilac® ABS-EX1000 High Impact Extrusion Grade ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trilac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trilac® ABS-EX1000 High Impact Extrusion Grade ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ASTM D638 |
| Flexural Yield Strength | 59.1 MPa | 8570 psi | ASTM D790 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm @Thickness 6.35 mm |
5.51 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 3.58 J/cm @Thickness 3.17 mm |
6.71 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 204 °C | 400 °F | |
| Front Barrel Temperature | 216 °C | 420 °F | |
| Melt Temperature | 232 - 249 °C | 450 - 480 °F | Nozzle temp not greater than stock |
| Mold Temperature | 54.4 - 71.1 °C | 130 - 160 °F | |
| Drying Temperature | 82.2 - 87.8 °C | 180 - 190 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 55.2 - 82.7 MPa | 8000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging 2710 Amber 9360 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Polikim KESTLUB® Polyamide 6 + Lubricant
- PolyOne FireCon™ CPE 0883-01 RoHS BLACK Polyethylene, Chlorinated (CPE)
- Sichuan Deyang Haton® hs1237B Polyphenylene Sulfide Coating
- Wingate Alloys Nicro 45 Ultra High Strength Alloy Wear Plate
- Barlog Plastics KEBAFLOW MF130 LCP, 30% glass fiber reinforced
- Bhansali Engineering Abstron IM-21 ABS Very High Rigidity Injection Molding Grade
- 3M FV035 Indoor UL Recognized White Vinyl Label Products
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with DOA
- Trelleborg Commercial Neoprene® C803 Chloroprene
Copyright © lookpolymers.com All Rights Reserved