- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 74.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 74.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ISO 75-1 |
| Mytex Polymers AS78L(W)-GM-02 Polypropylene, Rubber modified, Compounded Description: AS78L(W)-GM-02 is a compounded, rubber modified polypropylene with good impact and excellent material flow properties.Key Applications: Bumper fascias and all other exterior partsInform.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PP 1398 Conductive Thermoplastic Compound PRE-ELEC® PP 1398 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Petromont 5000 High Density Polyethylene Resin Petromont HDPE 5000 is a high density polyethylene copolymer resin produced using the UNIPOL™ Process. This resin is intended for use in prime sheet and thermoforming applications such as arena boa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | Unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CR350CS-01 Polypropylene Random Copolymer COPYLENE® CR350CS-01 is a clarified, reactor grade, random copolymer specially designed for clear injection molding applications and is formulated with lube for excellent mold release for larger ar.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Chevron Phillips HiD® 9412/HiD® 9413 with Antistat HDPE Blow Molding Resin
(discontinued **) Resin Type: Linear Copolymer; Blow Molding, Injection Blow Molding ResinCharacteristics: Medium Molecular Weight Distribution, Reduced Yellow Potential, Wide Range of Processing Conditions, Good Flo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Chevron Phillips HiD® 99413F with Food Grade Antistat HDPE Blow Molding Resin
(discontinued **) Resin Type: Linear Copolymer; Blow Molding, Injection Blow Molding ResinCharacteristics: Medium Molecular Weight Distribution, Reduced Yellow Potential, Wide Range of Processing Conditions, Good Flo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | no specified load; ASTM D648 |
| Formosa Plastics Formolene® DB5305A Blow Molding HDPE
(discontinued **) Extra High Molecular Weight Polyethylene Formolene® DB5305A is tailored for large part blow molding applications. Besides having excellent chemical resistance properties Formolene® DB5305A HDPE ha.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | Method A; ASTM D648 |
| Chevron Phillips Marlex® C516 HDPE Blow Molding Resin
(discontinued **) Resin Type: Hexene CopolymerCharacteristics: Outstanding impact resistanceOutstanding creep resistanceExcellent ESCRExcellent chemical resistanceExcellent melt stabilityApplications: 55 gallon drums.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| LyondellBasell Alathon® H5520 High Density Polyethylene ApplicationsALATHON H 5520 provides good processing characteristics and exhibits excellent toughness and color as well as low odor and good molded-part stability. Typical applications include house.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| LyondellBasell Petrothene® LB5604 High Density Polyethylene ApplicationsThe PETROTHENE LB 5604 series of polyethylene resins exhibits good stiffness and environmental stress cracking resistance. Typical applications include household chemical and person car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Ineos HP55-25-155 HDPE A high performance high density polyethylene copolymer developed for blow molding. It is recommended for use in continuous extrusion blowmolding equipment, specifically where applications require ex.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Ineos T50-3600 HDPE Ineos T50-3600 is a high density polyethylene copolymer of narrow molecular weight distribution used primarily for high speed injection molding of thin-walled articles. It is characterized by a hig.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP FL004 PE LNP* Lubricomp* FL004 is a compound based on Polyethylene resin containing 20% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY M3000C PP LNP* STAT-LOY* M3000C is a compound based on unfilled Polypropylene resin. Added features of this grade include: Clean Compound System, Antistat. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 394 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 394 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 394 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Eastman DuraStar MN610 Polymer, Natural Durastar MN610 polymer has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. MN610 has very .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Eastman Eastar MN004 Copolyester Eastar Copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN004 contains a mold release.Appl.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Eastman Spectar® 14471 Copolyester Spectar copolyester extrudes into plastic sheet that is sparkling clear, tough, chemically resistant, odor-free, versatile, easy to work with and affordable. Its toughness allows fabricators to use .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Entec Hypro™ PP-RP12/1.5C Random Clarified Copolymer, 12 Melt Flow This product is intended for injection molding applications that require fast cycle time, enhanced processability and excellent clarity. This product offers improved impact and utilizes the latest g.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 - 80.0 °C | 165 - 176 °F | with 160ºC thermal postcure; ASTM D648 |
| 3D Systems Accura® 50 Plastic for SLA® Systems Simulate the properties and appearance of molded ABS. For use with the Viper™ SLA® system, SLA 3500, SLA 5000 and SLA 7000 systems.ApplicationsFunctional components for assemblies, mock-ups and te.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM-D648 |
| Braskem GM8250T HDPE High Density Extrusion Polyethylene GM8250T is a high-density polyethylene specially developed for the manufacturing of corrugated pipes. It has high molar mass and shows excellent tenacity, high stiffness, good impact resistance, and.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Braskem Green PE SHA7260 Injection Molding High Density Polyethylene Description: SHA7260 is a high-density polyethylene, developed for the injection molding, easy to process and with high productivity. This resin has a good melt flow with high rigidity and hardness... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM-D648 |
| Braskem Prisma 2400 RACO Random Polypropylene Copolymer Prisma 2400 is a high melt flow rate random copolymer. This product is designed for the ISBM (Injection Stretch Blow Molding) process and offers low taste/odor. It can also be used in the blow moldi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM-D648 |
| Braskem HA7260 HDPE Injection Molding Polyethylene HA7260 is a high-density polyethylene that was developed for injection molding. It is easy to process and has high productivity, high rigidity and hardness, and a good melt flow. Its narrow molar ma.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| ExxonMobil HD 8760.29 Rotational Molding Resin Product Description: HD 8760 is a high density hexene copolymer designed to offer outstanding stiffness and processability. This resin is ideally suited for applications that require the optimum bal.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| ExxonMobil Paxon™ AS55-003 Blow Molding Resin
(discontinued **) AS55-003 is a blow molding grade high density polyethylene copolymer containing an antistat additive. It provides a good balance of stiffness and stress crack resistance.Information provided by Exx.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| ExxonMobil Paxon™ AU55-003 Blow Molding Resin
(discontinued **) AU55-003 is a blow molding grade high density polyethylene containing an excellent antistat additive, offering a good combination of stiffness and stress crack resistance. An enhanced additive pack.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Braskem BU 004 HDPE Blow Molding Polyethylene Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem |
|||