Braskem Prisma 2400 RACO Random Polypropylene Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	Braskem
Trade Name	Prisma
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem Prisma 2400 RACO Random Polypropylene Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Prisma 2400 is a high melt flow rate random copolymer. This product is designed for the ISBM (Injection Stretch Blow Molding) process and offers low taste/odor. It can also be used in the blow molding process. Its applications include: injection of transparent parts for packages; and ISBM technology transparent bottles for mineral water, teas, cold juices, drinks, and isotonic beverages.

Physical Properties	Metric	English	Comments
Density	0.902 g/cc	0.0326 lb/in³	ASTM-D792
Melt Flow	20 g/10 min @Load 2.16 kg, Temperature 230 °C	20 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM-D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	71	71	ASTM-D785
Tensile Strength, Yield	28.0 MPa	4060 psi	ASTM-D638
Elongation at Yield	16 %	16 %	ASTM-D638
Flexural Modulus, 1% Secant	900 MPa	131000 psi	ASTM-D790
Izod Impact, Notched	0.160 J/cm @Temperature -20.0 °C	0.300 ft-lb/in @Temperature -4.00 °F	ASTM-D256
	0.380 J/cm @Temperature 23.0 °C	0.712 ft-lb/in @Temperature 73.4 °F	ASTM-D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	74.0 °C	165 °F	ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi)	47.0 °C	117 °F	ASTM-D648
Vicat Softening Point	127 °C @Load 1.02 kg	261 °F @Load 2.25 lb	ASTM-D1525

Optical Properties	Metric	English	Comments
Haze	12 % @Thickness 1.00 mm	12 % @Thickness 0.0394 in	ASTM-D1003
Transmission, Visible	90 %	90 %	transparent; thickness not quantified