Chevron Phillips Marlex® C516 HDPE Blow Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Marlex® C516 HDPE Blow Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: Hexene CopolymerCharacteristics: Outstanding impact resistanceOutstanding creep resistanceExcellent ESCRExcellent chemical resistanceExcellent melt stabilityApplications: 55 gallon drumsIndustrial tanksInformation provided by Chevron Phillips.

Physical Properties	Metric	English	Comments
Density	0.954 g/cc	0.0345 lb/in³	ASTM D1505
ESCR 100% Igepal®	>= 1000 hour	>= 1000 hour	Conditions A and B; ASTM D1693
Melt Flow	5.5 g/10 min	5.5 g/10 min	Condition 190/2.16, HLMI; ASTM D1505

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	60	60	ASTM D2240
Tensile Strength, Yield	29.0 MPa	4210 psi	2 in/min, Type IV bar; ASTM D638
Elongation at Break	800 %	800 %	2 in/min, Type IV bar; ASTM D638
Flexural Modulus	1.31 GPa	190 ksi	Tangent, 16:1 span:depth,0.5in/min; ASTM D790
Tensile Impact Strength	450 kJ/m²	214 ft-lb/in²	Type S bar; ASTM D1822

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	74.0 °C	165 °F	Method A; ASTM D648
Vicat Softening Point	126 °C	259 °F	Loading 1, Rate A; ASTM D1525
Brittleness Temperature	<= -75.0 °C	<= -103 °F	Type A, type 1 specimen; ASTM D746