Formosa Plastics Formolene® DB5305A Blow Molding HDPE (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Formosa Plastics Formolene® DB5305A Blow Molding HDPE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Extra High Molecular Weight Polyethylene Formolene® DB5305A is tailored for large part blow molding applications. Besides having excellent chemical resistance properties Formolene® DB5305A HDPE has outstanding environmental stress crack resistance properties and exceptional impact and creep resistance. Formolene® DB5305A meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520(c) 3.2a, covering safe use of polyolefin articles intended for direct food contact. Formolene® DB5305A also meets all requirements of ASTM D4976-95 – PE 235.Applications: 55-Gallon, Drums Heavy Gauge Sheet, Industrial Tanks and Large Diameter Corrugated PipePhysical properties reported herein were determined on compression molded specimens prepared in accordance with Procedure C of ASTM D1928.Information provided by Formosa Plastics Corporation, USA

Physical Properties	Metric	English	Comments
Density	0.954 g/cc	0.0345 lb/in³	ASTM D1505
ESCR 100% Igepal®	>= 1000 hour	>= 1000 hour	Condition B, F<sub>50</sub>; ASTM D1693
Melt Flow	5.5 g/10 min @Load 2.16 kg, Temperature 190 °C	5.5 g/10 min @Load 4.76 lb, Temperature 374 °F	Condition F; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	29.0 MPa	4200 psi	2" (50mm) per min, Type IV; ASTM D638
Elongation at Break	>= 600 %	>= 600 %	2" (50mm) per min, Type IV; ASTM D638
Flexural Modulus	1.34 GPa	195 ksi	ASTM D790
Tensile Impact Strength	451 kJ/m²	215 ft-lb/in²	ASTM D1822

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	74.0 °C	165 °F	no specified load; ASTM D648
Vicat Softening Point	126 °C	259 °F	ASTM D1525
Brittleness Temperature	<= -70.0 °C	<= -94.0 °F	ASTM D746