Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 248 - 250 °C | 478 - 482 °F | PEPL-10-W-19 |
Pearl Engineering PEPLPET B-105C PET Bottle Grade A co-polymer used for soft drinks and other applications. |
|||
Melting Point | 200 - 250 °C | 392 - 482 °F | Average value: 224 °C Grade Count:18 |
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45.. |
|||
Melting Point | 248 - 250 °C | 478 - 482 °F | PEPL-10-W-19 |
Pearl Engineering PEPLPET B-07C PET Bottle Grade A co-polymer used mostly for containers. |
|||
Melting Point | 248 - 250 °C | 478 - 482 °F | PEPL-10-W-19 |
Pearl Engineering PEPLPET B-101C PET Sheet Grade A sheet grade polymer used in thick films. |
|||
Melting Point | 185 - 250 °C | 365 - 482 °F | |
Indium Corp. Indalloy® 138 Pb-Sn-Sb Solder Alloy Information provided by the manufacturer, Indium Corporation. |
|||
Melting Point | 246 - 250 °C | 475 - 482 °F | ZIMMER WN-B010-7089E |
Iran Petrochemical (PCC) PET BG-781 Polyethylene Terephthalate Polyethylene Terephthalate bottle grade chips (highly viscous ) is a condensation polymer produced by a continuous meltphase polymerization process followed by a solid state polymerization process. .. |
|||
Melting Point | 246 - 250 °C | 475 - 482 °F | ZIMMER WN-B010-7089E |
Iran Petrochemical (PCC) PET BG-800 Polyethylene Terephthalate Polyethylene Terephthalate bottle grade chips (highly viscous ) is a condensation polymer produced by a continuous meltphase polymerization process followed by a solid state polymerization process. .. |
|||
Melting Point | 246 - 250 °C | 475 - 482 °F | ZIMMER WN-B010-7089E |
Iran Petrochemical (PCC) PET BG-821 Polyethylene Terephthalate Polyethylene Terephthalate bottle grade chips (highly viscous ) is a condensation polymer produced by a continuous meltphase polymerization process followed by a solid state polymerization process. .. |
|||
Melting Point | 230 - 250 °C | 446 - 482 °F | |
Johnson Matthey JM 97C Soft Solder/Flux General information on the Johnson Matthey soft solder and flux product line: A wide range of Tin/Lead solders suitable for a variety of applications is available from Johnson Matthey. Most materi.. |
|||
Melting Point | 185 - 250 °C | 365 - 482 °F | |
Johnson Matthey JM3070 Soft Solder/Flux General information on the Johnson Matthey soft solder and flux product line: A wide range of Tin/Lead solders suitable for a variety of applications is available from Johnson Matthey. Most materi.. |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1, -3 |
Lanxess Pocan® ECO T 3215 000000 PBT + PET, 15% Glass Fiber PBT + PET, 15% glass fibers, injection molding, improved surface finish, contains 30% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS. |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1, -3 |
Lanxess Pocan® ECO T 3220 000000 PBT + PET, 20% Glass Fiber PBT + PET, 20% glass fibers, injection molding, improved surface finish, contains 28% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS. |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1, -3 |
Lanxess Pocan® ECO T 3230 000000 PBT + PET, 30% Glass Fiber PBT + PET, 30% glass fibers, injection molding, improved surface finish, contains 30% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS. |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1, -3 |
Lanxess Pocan® ECO T 3240 000000 PBT + PET, 45% Glass Fiber PBT + PET, 45% glass fibers, injection molding, improved surface finish, contains 25% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS. |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 |
Lanxess Pocan® KU 1-7313 000000 PBT + PET, 15% Glass Fiber PBT+PET, 15% glass fibers, injection molding, improved surface finish, increased temperature peak load |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 |
Lanxess Pocan® T 7331 000000 PBT + PET, 30% Glass Fiber PBT+PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1, -3 |
Lanxess Pocan® T 7331 POS151 700226 PBT + PET, 30% Glass Fiber PBT + PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV stabilizedInformation provided by LANXESS. |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 |
Lanxess Pocan® T 7391 000000 PBT + PET, 45% Glass Fiber PBT+PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 |
Lanxess Pocan® T 7323 000000 PBT + PET, 20% Glass Fiber PBT+PET, 20% glass fibers, injection molding, improved surface finish, increased temperature peak load |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 |
Lanxess Pocan® T 7323 POS151 000000 PBT + PET, 20% Glass Fiber PBT+PET, 20% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10 K/min; ISO 3146 |
Eurotec® Tecodur® PB70 GR30 NL CA 01 PBT/PET 30% glass fiber reinforced Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance.. |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10 K/min; ISO 3146 |
Eurotec® Tecodur® PB70 GR20 NL CA 01 PBT/PET 20% glass fiber reinforced Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance.. |
|||
Melting Point | 220 - 250 °C | 428 - 482 °F | |
BASF Ultradur B 4040 G10 BK5110 50% Glass Filled PBT Injection-molding grades containing 50% of glass fibers, for industrial parts with excellent surface quality.Applications: External door handles in vehicles, visible sunroof frames, over door handle.. |
|||
Melting Point | 220 - 250 °C | 428 - 482 °F | ISO 11357-3 |
BASF Ultradur B 4300 G4 20% Glass Filled PBT Ultradur B4300 G4 is an easy flowing injection molding PBT with 20% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.Applications: Program switches, thermostat parts, small.. |
|||
Melting Point | 220 - 250 °C | 428 - 482 °F | DSC; ISO 11357-3 |
BASF Ultradur® B 4040 G2 10% Glass Filled PBT + PET Description: Is a PBT + PET, injection-molding grade containing 10% of glass fibers, for industrial parts, rigid, tough and dimensionally stable, for example for program switches, thermostat parts, .. |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 |
Lanxess Pocan® TS 3220 901510 PBT + PET, 20% Glass Fiber PBT+PET, 20% glass fibers, injection molding, impact modified, low tendency to warp, improved surface finish |
|||
Melting Point | 220 - 250 °C | 428 - 482 °F | DSC; ISO 11357-3 |
BASF Ultradur® B 4040 G4 20% Glass Filled PBT + PET PBT + PET, injection-molding grade containing 20% of glass fibers, for industrial parts, rigid, tough and dimensionally stable, for example for program switches, thermostat parts, small-motor housin.. |
|||
Melting Point | 220 - 250 °C | 428 - 482 °F | DSC; ISO 11357-3 |
BASF Ultradur® B 4040 G6 30% Glass Filled PBT + PET PBT + PET, injection-molding grade containing 30% of glass fibers, for industrial parts, rigid, tough and dimensionally stable, for example for program switches, thermostat parts, small-motor housin.. |
|||
Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 |
Lanxess Pocan® A 3131 000000 PBT+ASA, 30% glass fibers PBT+ASA, 30% glass fibers, injection molding, low tendency to warp, improved surface finish |