Lanxess Pocan® TS 3220 901510 PBT + PET, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® TS 3220 901510 PBT + PET, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT+PET, 20% glass fibers, injection molding, impact modified, low tendency to warp, improved surface finish
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.364 g/cc | 0.04928 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Melt Flow | 25 g/10 min @Load 5.00 kg, Temperature 270 °C |
25 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-1/-2 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 |
| Tensile Modulus | 5.60 GPa | 812 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Impact | 2.1 | 2.1 | Puncture maximum force (N); ISO 6603-2 |
| 1.6 @Temperature -30.0 °C |
1.6 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.70 J | 1.99 ft-lb | ISO 6603-2 |
| 1.80 J @Temperature -30.0 °C |
1.33 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 72.0 °C | 162 °F | ISO 75-1/-2 |
| Vicat Softening Point | 150 °C | 302 °F | 50°C/h 50N; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 °C | 518 °F | Injection Molding; ISO 294 |
| Mold Temperature | 90.0 °C | 194 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT+PET,GHLMPR,09-060,GF20 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 TF-GV 1530 Nylon 6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced
- PEAK Werkstoff DISPAL S690 Aluminum Alloy, AlCu4MgAg, Condition T6
- Lehmann & Voss LUVOCOM® 1105-8476 PEEK, with carbon fiber
- Crucible Steel CPM® Rex® 54® (HS) High Speed Steel
- Eurostar Starpylen MFM43S PP, Glass/Mineral Filled, Injection Molded
- Asahi Glass Lumiflon LF-200 Solvent Soluble Fluoropolymer w/ isocyanate hardening agent
- Beijing Ranger Chem 197 Solid Epoxy Resin
- Abatron AboCast 50-11/AboCure 50-17 Epoxy
- ArcelorMittal HSLA 300 High strength low alloy steel for cold forming, Cold Rolled
Copyright © lookpolymers.com All Rights Reserved