Sumitomo Bakelite North America RX® 1-510N Mineral Filled Diallyl Phthalate

Category	Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP), Cast, Mineral Filler , Filled/Reinforced Thermoset
Manufacturer	Sumitomo Bakelite North America
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sumitomo Bakelite North America RX® 1-510N Mineral Filled Diallyl Phthalate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Information provided by Sumitomo Bak North America, Inc.

Physical Properties	Metric	English	Comments
Density	1.66 g/cc	0.0600 lb/in³	ASTM D792
Apparent Bulk Density	0.690 g/cc	0.0249 lb/in³
Water Absorption	0.50 %	0.50 %	48 hours, 50°C. ASTM D570
Linear Mold Shrinkage	0.0030 - 0.0060 cm/cm	0.0030 - 0.0060 in/in	Compression Molding. ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	52.0 MPa	7540 psi	ASTM D638
Flexural Yield Strength	97.0 MPa	14100 psi	ASTM D790
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Compressive Yield Strength	138 MPa	20000 psi	ASTM D695
Izod Impact, Notched	0.240 J/cm	0.450 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	29.0 µm/m-°C @Temperature 20.0 °C	16.1 µin/in-°F @Temperature 68.0 °F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	163 °C	325 °F	ASTM D648A

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.7 @Frequency 1e+6 Hz	3.7 @Frequency 1e+6 Hz	Wet
	4.2 @Frequency 1000 Hz	4.2 @Frequency 1000 Hz	Wet
Dielectric Strength	15.0 kV/mm	381 kV/in	Wet, step-by-step. ASTM D149
	16.0 kV/mm	406 kV/in	Wet, short term. ASTM D149
Dissipation Factor	0.015 @Frequency 1000 Hz	0.015 @Frequency 1000 Hz	Wet; ASTM D150
	0.017 @Frequency 1e+6 Hz	0.017 @Frequency 1e+6 Hz	Wet; ASTM D150
Arc Resistance	135 sec	135 sec	ASTM D495

Processing Properties	Metric	English	Comments
Processing Temperature	160 - 180 °C	320 - 356 °F	Mold temperature