SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* UF006H is a compound based on Polyphthalamide resin containing Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0037 cm/cm @Time 86400 sec |
0.0037 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0077 cm/cm @Time 86400 sec |
0.0077 in/in @Time 24.0 hour |
ISO 294 |
| 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 208 MPa | 30200 psi | ISO 527 |
| 224 MPa | 32500 psi | ASTM D638 | |
| Tensile Strength, Yield | 208 MPa | 30200 psi | ISO 527 |
| 224 MPa | 32500 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Tensile Modulus | 12.44 GPa | 1804 ksi | 1 mm/min; ISO 527 |
| 13.1 GPa | 1900 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 289 MPa | 41900 psi | ASTM D790 |
| 294 MPa | 42600 psi | ISO 178 | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| 11.03 GPa | 1600 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.83 J/cm | 12.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m² | 22.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 51.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 28.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 28.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 293 °C | 559 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 305 °C @Thickness 3.20 mm |
581 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 282 °C | 540 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 287 °C @Thickness 3.20 mm |
549 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Industrial Laminates/Norplex NP509 Glass Fabric
- Lanxess Durethan® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified
- Solvay Specialty Polymers Algoflon® L203F Polytetrafluoroethylene (PTFE)
- Samyang Triel® 5552EM Thermoplastics Polyetherester Elastomer, Extrusion
- Saint-Gobain Norton® PMP Film
- SABIC Innovative Plastics LNP THERMOCOMP TF002 PU
- Dow Corning SYL-OFF® 7367 CROSSLINKER
- Crucible Steel Cru-Wear® Tool Steel
- Fainplast Compounds GA 89/3 Flexible PVC, Flame Retardant Sheathing
- Azoty Tarnow™ Alphalon™ 32 Nylon 6
Copyright © lookpolymers.com All Rights Reserved