- PolyOne Lubri-Tech™ PS-30GF/ 02S PBT Polyester - 30% Glass Fiber - 2% Silicone (discontinued **)
PolyOne Lubri-Tech™ PS-30GF/ 02S PBT Polyester - 30% Glass Fiber - 2% Silicone (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PS-30GF/ 02S PBT Polyester - 30% Glass Fiber - 2% Silicone
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.523 g/cc | 0.05502 lb/in³ | ASTM D792 |
| Water Absorption | 0.17 % | 0.17 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0025 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 103 MPa | 14900 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ASTM D638 |
| Flexural Yield Strength | 159 MPa | 23100 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 - 1.33 J/cm @Thickness 6.35 mm |
1.80 - 2.49 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 271 °C | 460 - 520 °F | Stock |
| Mold Temperature | 93.0 - 121 °C | 199 - 250 °F | |
| Drying Temperature | 93.0 °C | 199 °F |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8961F (896-1) (UF) Synthetic Oil
- SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS (Asia Pacific)
- Radici Heraflex® E 7722 TPC-ET Thermoplastic Elastomer
- Gouda Vuurvast CURON 160 H SIC GM Dense Refractory Castable
- TIMCAL TIMREX® LSG6 Natural Graphite
- TIMET TIMETAL® 3-2.5 Titanium Alloy (Ti-3Al-2.5V; ASTM Grade 9) Annealed
- Eagle Brass 706 Copper Nickel 10%, Extra Hard
- Eastman Tenite Butyrate 576E3720010 Clear, Trsp Cellulose Acetate Butyrate
- BASF Ultramid® C40 LN 07 0.04 mm Blown Film Cold Air
- Bhansali Engineering Abstron KU660 ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved