SABIC Innovative Plastics LNP THERMOCOMP RX09411H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX09411H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX09411H is a compound based on Nylon 66 containing Proprietary Fillers. Characteristics are: Radiopacity and Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.630 % | 0.630 % | 50% RH, 24 hrs; ASTM D570 |
| 0.920 % | 0.920 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 184 MPa | 26700 psi | 5 mm/min; ISO 527 |
| 188 MPa | 27300 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.32 GPa | 1787 ksi | 1 mm/min; ISO 527 |
| 12.6 GPa | 1830 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 264 MPa | 38300 psi | ISO 178 |
| 275 MPa | 39900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 11.03 GPa | 1600 ksi | 2 mm/min; ISO 178 |
| 11.5 GPa | 1670 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.710 J/cm | 1.33 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.82 J/cm | 14.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® P-650R Polyester Prepreg, 7781 E-Glass Reinforced
- PolyOne Elastamax™ EG-9065 Thermoplastic Elastomer (TPE)
- S&E Specialty Polymers TufTech™ GM-94-106D PVC Compound
- SABIC Innovative Plastics Valox® 364 PBT (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP DX10313 PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP PB006EQ PA 6 (Europe-Africa-Middle East)
- A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT
- EMS-Grivory Grivory® BG-30 FR PA6-GF30 FR
- ConocoPhillips Synterra™ 1 Hydraulic Oil, AGMA No. 1
- ACC MM282 Specialist Molding 2-Part Condensation Cure