Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 5.10 GPa | 740 ksi | Tangent; ASTM D790 |
RheTech Products F38-04 35% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, White Applications: HousingsBracketsSupport ductsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ASTM D790 |
Niche Polymer PPCG40BK Copolymer PP, 40% Glass Fiber Filled Information provided by Niche Polymer |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ASTM Data |
BASF Capron® SEG3 H1 15% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron SEG3 H1 is a 15% glass reinforced nylon 6 injection molding compound exhibiting. It exhibits exceptional surface aesthetics at the slower fill speeds associated with the gas assist injection .. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ASTM D790 |
LATI LATAN 13 G/15 15% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM)
(discontinued **) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
Flexural Modulus | 5.10 - 9.31 GPa | 740 - 1350 ksi | Average value: 7.66 GPa Grade Count:17 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%.. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 2 mm/min; ISO 178-A |
Lanxess Durethan® BKV 115 H2.0 DUS008 000000 Nylon 6, 15% Glass Fiber PA 6, 15% glass fibers, injection molding, impact modified, heat-ageing stabilizedInformation provided by LANXESS. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2212EPR PEI 20% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA lising. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2212R PEI 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2212R PEI (Asia Pacific) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 815F PBT+PET (Europe-Africa-Middle East) PBT+PET, 15% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | |
Shinil Chemical SHINSTRA PC/PET TES Structural Polymer Car Spoiler SHINSTRA is the product line of structural polymer compound which exhibits excellent physical, mechanical, and thermal properties. Shinil uses the state-of-the-art dispersion and blending technolog.. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP MF006SXP PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MF006SXP is a compound based on Polypropylene resin containing Glass Fiber. Added features include: Chemically Coupled. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp MFM43S PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MFM43S is a compound based on Polypropylene resin containing Glass Fiber, Mineral. Added features include : Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-.. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ASTM D790 |
Chase Plastics CP Pryme® N140MGHSL (COND, 50% RH) Nylon 6, 40% Mineral/Glass Reinforced, Heat Stabilized, Internally Lubricated Information provided by Chase Plastics. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ISO 178-93 |
Wellman Wellamid® GF13-66 22LH-NBK1 13% Glass Fiber Reinforced, General Purpose Nylon 66 Description: Glass Fiber Reinforced, General Purpose Nylon 66Information provided by Wellman. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 2mm/min; ISO 178 |
Borealis Xmod™ GD302HP Polypropylene, Glass Fiber Reinforced Xmod™ GD302HP is a 30 % chemically coupled high performance glass fiber reinforced polypropylene compound intended for injection molding. This material has an excellent balance between impact stre.. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ASTM D790 |
Asahi Kasei Thermylene® P6-30FG-0153 30% Glass Fiber Reinforced, Chemically Coupled Information provided by Asahi Thermofil |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ISO Data |
BASF Ultramid® 8231G HS BK-106 14% Glass Filled PA6 (Dry) Ultramid 8231G HS BK-106 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes.. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ASTM D790 |
Asahi Kasei Thermylene® P6-30FG-0632 30% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ISO Data |
BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Conditioned) Ultramid 1703-2 BK ND3007 is a 25% glass reinforced, heat stabilized injection molding nylon 6/6. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | STN EN ISO 178 |
Plastcom SLOVASTER® B GB 40 PBT reinforced with glass beads PBT for injection molding, reinforced with 40% glass beads. Characterized by very good properties also at low temperature. Melt is characterized by very good rheology, which enables manufacturing of.. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® K4530 PBT 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON ME003S PP (Asia Pacific) LNP STAT-KON* ME003S is a compound based on Polypropylene resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Modulus | 5.10 GPa | 740 ksi | ASTM-D790 |
Polyram RamSter PF303G4 PBT, 20% Glass Fiber 20% Glass-fiber reinforced, low viscosity PBT for injection molding applications.Information provided by Polyram Ram On Ind. |