SABIC Innovative Plastics LNP Thermocomp MFM43S PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MFM43S PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MFM43S is a compound based on Polypropylene resin containing Glass Fiber, Mineral. Added features include : Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % @Temperature 23.0 °C, Time 86400 sec |
0.010 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 3.7 % | 3.7 % | Flexural Strain, 2 mm/min; ISO 178 | |
| Tensile Modulus | 5.40 GPa | 783 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.10 GPa | 740 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 44.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
24.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 127 µm/m-°C @Temperature 23.0 - 60.0 °C |
70.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFill™ GPE3003-70 Natural Flame Retardant concentrate in LLDPE
- SABIC Innovative Plastics Lexan® 243R PC (Asia Pacific)
- SABIC Innovative Plastics Lexan® FXD9810U PC Copolymer (Asia Pacific)
- Teknor Apex Tekbond® TB 1372A Thermoplastic Elastomer
- Wieland Auropal 50 Casting Alloy
- Total PPC 3666 Polypropylene, Heterophasic Copolymer, Extrusion
- Chevron Phillips Marlex® HXB TR-512 Extra high molecular weight polyethylene
- DuPont™ Surlyn® 1857 Zinc Ionomer Resin for Blown and Cast Film
- Americas Styrenics STYRON® 666D High Heat Crystal Polystyrene
- Ashley Polymers Ashlene® 830LS-30G Nylon 6, 30% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved