Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 4.90 GPa | 711 ksi | 1% Secant at 0.05 in/min; ASTM D790 |
North Wood Plastics Polypropylene with 60% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc. |
|||
Flexural Modulus | 4.90 - 13.0 GPa @Temperature 100 - 175 °C |
711 - 1890 ksi @Temperature 212 - 347 °F |
Average value: 7.76 GPa Grade Count:1 |
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi.. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
PolyOne Nymax™ GF 1200 A 13 Natural Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | Secant; ASTM D790 |
Fiberfil® FPI-15 BK Nylon 6, 15% Glass Reinforced, post industrial Information provided by FIBERFIL Engineered Plastics |
|||
Flexural Modulus | 4.90 GPa @Thickness 3.20 mm |
711 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical LUCON CP6080LP PC+CNT+GF Description: Injection Molding, PC+CNT+GF, Electrostatic Dissipation, Low Surface TribochargeApplication: ATM parts, HDD BracketCAS No. 103598-77-2, 65997-17-3 and 7782-42-5Information provided by L.. |
|||
Flexural Modulus | 4.90 GPa @Thickness 6.40 mm |
711 ksi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
LG Chemical LUMID GP2101BF PA66+GF10%, Halogen Free Flame Retardant Feature: Injection Molding, PA66+GF10%, Halogen Free Flame RetardantApplication: ConnectorsCAS No. 32131-17-2, 25038-54-4, 65997-17-3, 88497-56-7, 1309-64-4 and 138265-88-0Information provided by LG.. |
|||
Flexural Modulus | 4.90 GPa @Thickness 3.20 mm |
711 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2130B(W) PA66+GF13%, General Purpose Feature: Injection Molding, PA66+GF13%, General PurposeApplication: Valve CoversCAS No. 32131-17-2, 65997-17-3 and 9010-79-9Information provided by LG Chemical |
|||
Flexural Modulus | 4.90 GPa @Thickness 3.20 mm |
711 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP3300B(W) PA66+MF30%, General Purpose Feature: Injection Molding, PA66+MF30%, General PurposeApplication: Automotive (Engine Cover))CAS No. 25038-54-4 and 9010-79-1Information provided by LG Chemical |
|||
Flexural Modulus | 4.90 GPa @Thickness 3.20 mm |
711 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOS GP2206F ABS+GF20%, Flame Retardant Feature: Injection Molding, ABS+GF20%, Flame RetardantApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9, 9003-54-7, 65997-17-3, 88497-56-7 and 1309-64-4Information provided b.. |
|||
Flexural Modulus | 4.90 GPa @Thickness 3.20 mm |
711 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical Lupox® SG3250A PBT+PET+MF25% Description: Injection Molding, PBT+PET+MF25%, Good SurfaceApplication: Automotive (Head Lamp Bezel)CAS No. 24968-12-5, 25038-59-9 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
IRPC Polimaxx Polene 2511HX GA5 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 25% GLASS FIBRE REINFORCED VERY HIGH IMPACT STRENGTH, HIGH MECHANICAL STRENGTH, LOW SHRINKAGE, HIGH STIFFNESS, CONTAIN UV STABILIZER AND LONG TERM.. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | cond., 2 mm/min; ISO 178-A |
Lanxess Durethan® BKV 130 GIT DUS008 900116 Nylon 6, Impact Modified PA 6, 30% glass fibers, injection molding, impact modified, GIT/WITInformation provided by LANXESS. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | cond., 2 mm/min; ISO 178-A |
Lanxess Durethan® DP BKV 30 XF 000000 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, injection molding, improved flowability, improved surface finishInformation provided by LANXESS. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
LG Chemical LUPOS GP-2200H General Purpose ABS, 20% Glass Fiber Reinforced, High Heat Resistance LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have .. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | 2 mm/min; ISO 178-A |
Lanxess Durethan® BKV 115 DUS008 000000 Nylon 6, 15% Glass Fiber PA 6, 15% glass fibers, injection molding, impact modified, heat-ageing stabilizedInformation provided by LANXESS. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | 2 mm/min; ISO 178-A |
Lanxess Durethan® BKY 115 H3.0 DUS008 Nylon 6, 15% Glass Fiber PA 6, 15% glass fibers, injection molding, impact modified, heat-ageing stabilizedInformation provided by LANXESS. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Lubricomp KFL22 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KFL22 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP f.. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® GP-5150GT PBT, 15% Glass Filled Low warpage with 15% GF reinforcement and can be used in the switches for microwave or ovensInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
Samyang Trirex® 3500G20 Polycarbonate, 20% Glass Reinforced TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® P305G30 PP, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ISO 178-93 |
Wellman Wellamid® GF14-60 XE-NBK1 Nylon 6, 14% Glass Fiber Reinforced All information provided by Wellman Engineered Resins. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ISO 178 |
Wellman Wellamid® MR340 42H-N 34% Mineral Reinforced Nylon 6, Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66
(Unverified Data**) 13% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G13HS1L NC010 is a 13% glass fiber reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Perfor.. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
Ashley Polymers Ashlene® P265WO PPO, 20% Glass Reinforced A general purpose, 20% glass reinforced flame retardant, PPO resin for injection molding applications requiring structural strength, dimensional stability and good heat resistance.Data provided by t.. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
Gromax PBT 3015-104 15% Glass Fiber Filled Product Description: A glass fiber 15% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent .. |
|||
Flexural Modulus | 4.90 GPa @Temperature 150 °C |
711 ksi @Temperature 302 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA)
(Unverified Data**) Amodel A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength.. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® GP-3200G PBT/ABS, 20% Glass Filled PBT/ABS with 20% GF reinforcement that can be used in air-conditioner bladesInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
Gromax CCP PBT 5615-104C 15% Glass Fiber Filled Product Description: A glass fiber 15% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent .. |
|||
Flexural Modulus | 4.90 GPa @Temperature 175 °C |
711 ksi @Temperature 347 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry
(discontinued **) Amodel A-4133L polyphthalamide (PPA) is a 33% glass reinforced resin designed to offer high crystallinity when molded in water-cooled molds. Key properties include high heat resistance, reduced outg.. |