Lanxess Durethan® BKV 130 GIT DUS008 900116 Nylon 6, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 130 GIT DUS008 900116 Nylon 6, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 30% glass fibers, injection molding, impact modified, GIT/WITInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00060 cm/cm | 0.00060 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0015 cm/cm | 0.0015 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0050 cm/cm | 0.0050 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 160 MPa | 23200 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 3.4 % | 3.4 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 7.5 % | 7.5 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 5.00 GPa | 725 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 9.00 GPa | 1310 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 145 MPa @Strain 6.30 % |
21000 psi @Strain 6.30 % |
cond., 2 mm/min; ISO 178-A |
| 256 MPa @Strain 4.10 % |
37100 psi @Strain 4.10 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 122 MPa @Strain 3.50 % |
17700 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 230 MPa @Strain 3.50 % |
33400 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 4.90 GPa | 711 ksi | cond., 2 mm/min; ISO 178-A |
| 8.50 GPa | 1230 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | d.a.m.; ISO 180-1A |
| 15.0 kJ/m² | 7.14 ft-lb/in² | cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1U |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1U | |
| 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1U | |
| 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1U | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eU |
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA | |
| Puncture Energy | 2.50 J @Load <=78.5 kg, Temperature -30.0 °C |
1.84 ft-lb @Load <=173 lb, Temperature -22.0 °F |
ISO 6603-2 |
| 3.80 J @Load <=95.3 kg, Temperature 23.0 °C |
2.80 ft-lb @Load <=210 lb, Temperature 73.4 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1, -2 |
| Vicat Softening Point | 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6-HI, GR, 14-090, GF30 |
Users viewing this material also viewed the following:
- SABIC PP 528K Polypropylene Homopolymer for Thermoforming
- Ravago Manufacturing Americas Hylex® P1325L Polycarbonate, UV Stabilized, High Flow, Mold Release
- Fine Organics FINALUX G 748 Lubricant Additive
- Ineos B4020N1332 Polyethylene Copolymer
- Solvay Specialty Polymers Ryton® R-4-232NA Polyphenylene Sulfide (PPS), 40% Glass Fiber
- SABIC Innovative Plastics LNP THERMOCOMP RF00C PA 66
- Polyplastics TOPAS® 5013 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade)
- Eurostar Starpylen MX06050 PP, 30% Glass Filled, Injection Molded
- RheTech Products M20P100-01A 20% Mica Reinforced Polypropylene, Black