- Samsung Cheil Industries Infino® GP-5150GT PBT, 15% Glass Filled
Samsung Cheil Industries Infino® GP-5150GT PBT, 15% Glass Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GP-5150GT PBT, 15% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low warpage with 15% GF reinforcement and can be used in the switches for microwave or ovensInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Temperature 23.0 °C |
0.070 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.011 cm/cm @Thickness 3.20 mm |
0.0040 - 0.011 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 250 °C |
25 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 91.2 MPa | 13200 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 98.1 MPa | 14200 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 4.41 GPa | 640 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 147 MPa | 21300 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 4.90 GPa | 711 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.353 J/cm @Thickness 6.35 mm |
0.661 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.490 J/cm @Thickness 3.17 mm |
0.918 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C @Thickness 6.40 mm |
423 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C @Thickness 6.40 mm |
365 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 200 °C | 392 °F | B/50; ISO R306 |
| 203 °C | 397 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 0.700 mm |
HB @Thickness 0.0276 in |
Users viewing this material also viewed the following:
- Grupo Repol Dinalon® B1S25 G25 25% Glass Fiber Reinforced Nylon 6
- Silikony Polskie Polsil Gum 100/50 HTV Silicone Rubber
- Styrolution Absolan® 2150 SAN
- Total PS CPDS 9217 Compound Polystyrene/Polyethylene
- A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer
- ExxonMobil LDPE LD 157CW Blown Low Density Polyethylene Resin
- 3M 616 Lithographers Tape
- Arlon 55986R028 0.0295" Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved