Asia International Enterprise (Hong Kong) 60T6 Nylon 66, 30% Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled
Manufacturer Asia Int'l Enterprise (Hong Kong) Limited
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asia International Enterprise (Hong Kong) 60T6 Nylon 66, 30% Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc

@Temperature 23.0 °C
 1.42 g/cc

@Temperature 73.4 °F
 ASTM D792
Filler Content 30 %
30 %
Linear Mold Shrinkage 0.0050 - 0.010 cm/cm
0.0050 - 0.010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ASTM D785
Tensile Strength, Ultimate 78.5 MPa
11400 psi
5mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
5mm/min; ASTM D638
Flexural Strength 98.1 MPa
14200 psi
2.8mm/min; ASTM D790
Flexural Modulus 4.90 GPa
711 ksi
2.8mm/min; ASTM D790
Izod Impact, Notched 0.196 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
 0.367 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 261 °C
502 °F
ASTM D789
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
ASTM D648
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Middle Barrel Temperature 250 - 300 °C
482 - 572 °F
Cylinder Temperature
Mold Temperature 50.0 - 90.0 °C
122 - 194 °F
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Dry Time 4 - 6 hour
4 - 6 hour