- Polymer Property : Flexural Modulus = 696 ksi
Polymer Property : Flexural Modulus = 696 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 4.80 GPa | 696 ksi | STN EN ISO 178 |
| Plastcom PLASTALEN® PH 69 GF 30 Polypropylene reinforced with glass fiber Modified homopolymer PP for injection molding, reinforced with 30% glass fiber. Applied in all industry branches. Delivered in natural mode and in the full RAL color scale.Information Provided by Pl.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP BX05030 SAN (Europe-Africa-Middle East) LNP* Lubricomp* BX05030 is a compound based on Styrene Acrylonitrile resin containing Mineral, Graphite. |
|||
| Flexural Modulus | 4.80 - 5.50 GPa @Temperature 90.0 - 90.0 °C |
696 - 798 ksi @Temperature 194 - 194 °F |
Average value: 5.15 GPa Grade Count:2 |
| Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Custom Resins Vexel™ 5100 RD PBT; 15% Glass Filled
(discontinued **) Improved Surface. Property data for dry as molded samples.Data provided by the manufacturer |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Resinoid 2205 Phenolic Molding, Cellulose Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||
| Flexural Modulus | 4.80 GPa @Temperature 23.0 °C |
696 ksi @Temperature 73.4 °F |
ISO 178 |
| Polykemi AB POLYlux 3809S F20 PC/PBT-Blend, Glass Fiber-Reinforced Information provided by Polykemi AB |
|||
| Flexural Modulus | 4.80 GPa @Temperature 90.0 °C |
696 ksi @Temperature 194 °F |
ISO 178, ASTM D790 |
| Nilit Nilamid A G5 FR C4 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Halogens) Description: Nilamid A G5 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ.. |
|||
| Flexural Modulus | 4.80 - 10.5 GPa | 696 - 1520 ksi | Average value: 8.22 GPa Grade Count:21 |
| Overview of materials for Phenolic, Novolac, Mineral/Flock Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Flock Filled". Each property range of values reported is minimum and maximum .. |
|||
| Flexural Modulus | 4.80 - 11.0 GPa | 696 - 1600 ksi | Average value: 7.41 GPa Grade Count:17 |
| Overview of materials for Phenolic, Novolac, Cellulose Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Cellulose Filled". Each property range of values reported is minimum and maximum valu.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Plenco 306 Black General Purpose Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok 306 is a two-stage, mineral and flock-filled phenolic molding compound designed to have the heat resistant characteristics of Plaslok 504, while at the same time, improved impact strength.Da.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO 178 |
| Grupo Repol Dinalon® B1S25 M404 PA6 40% Mineral Charge Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2110EPR PEI (Asia Pacific) 10% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON DDF029 PC (Asia Pacific) LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant, Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Sax Polymers SAXAMID 226F3 Nylon 6.6, 15% Glass Fiber SAXAMID 226F3 is a polyamide 6.6 injection-molding-grade reinforced with 15% glass fibers. This grade is suitable for applications requiring high strength and very good flow properties during proces.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP Thermocomp MFK42AS PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MFK42AS is a compound based on PP resin containing Glass Fiber, Mineral.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS (Asia Pacific) Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl .. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM-D790 |
| Polyram RamTough RZ300G4 Polycarbonate, 20% Glass Fiber 20% glass fiber reinforced polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM-D790 |
| Polyram PlusTek PB320G3 Nylon 6, 15% Glass Fiber, Flame Retardant 15% glass-fiber reinforced, flame retardant polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | DIN 52457 |
| CP-Polymer-Technik Wellamid® 6000/42 GV 15 HWCP 15% Glass Fiber Nylon 6, Polymer Modified, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | DIN 52457 |
| CP-Polymer-Technik Wellamid® 6000/58 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Flexural Modulus | 4.80 GPa @Temperature 23.0 °C |
696 ksi @Temperature 73.4 °F |
EN ISO 178 |
| Ensinger TECASINT 4041 Polyimide, Glossy Black, Molybdenum Sulfide (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Eurostar Staramide PF004EUC PA6, 20% Glass Filled, Injection Molded PF004EUC is a 20% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| E-Polymers TEKAMID® TB120G15 , 15% Glass Fiber Reinforced PA6, DAM 15% Glass Fiber reinforced, Good surface Information provided by E-Polymers Co. Ltd. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 528L-13G Nylon 66, 13% Glass Reinforced General purpose glass fiber reinforced Nylon 66, designed for parts requiring excellent thermal and dimensional stability and higher strength than conventional resins.Data provided by the manufactur.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 528LSB2-20G Nylon 66, 20% Glass Reinforced A UV Stabilized 20% glass fiber reinforced Nylon 66 designed for parts requiring excellent thermal and dimensional stability and higher strength than conventional resins.Data provided by the manufac.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | dry; ISO 178 |
| Azoty Tarnow™ Tarnamid® T-27 GF15 Polyamide 6 - Glass Fiber Reinforced 15% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Plaslok 306 Black General Purpose Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use. Plaslok 306 is a two-stage, mineral and flock.. |
|||
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Adell RQ-18 Copolymer Polypropylene, 40% Mica Reinforced Data provided by Adell Plastics, Inc. |
|||