- E-Polymers TEKAMID® TB120G15 , 15% Glass Fiber Reinforced PA6, DAM
E-Polymers TEKAMID® TB120G15 , 15% Glass Fiber Reinforced PA6, DAM
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers TEKAMID® TB120G15 , 15% Glass Fiber Reinforced PA6, DAM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Glass Fiber reinforced, Good surface Information provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 1.5 % | 1.5 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D786 |
| Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 170 MPa | 24700 psi | ASTM D790 |
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 160 sec | 160 sec | Tungsten electrode; ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA - 41 FDA General Purpose Acrylic Resin
- MV Labs PB1000 PbSO4 Lead(II) sulfate
- Polykemi AB POLYelast TPE Z900 Thermoplastic Elastomer, SEBS-based
- Flint Hills P4G3Z-039 Homopolymer Polypropylene
- Shakespeare WN-50 diameter 0.2 mm Nylon Monofilament 610
- Techmer ES HiFill FR® ASA FR-2A WT209
- Plenco 1530 Polyester, Briquette, Injection Molded
- ELASTO UK Dryflex® 650900 TPE, Improved Compression Set and High Temperature Resistance, 90A Hardness
- 3M Scotch-Weld™ MG300 FLX Medical Grade Instant Adhesive
- BASF Ultradur B 6550 PBT
Copyright © lookpolymers.com All Rights Reserved