- SABIC Innovative Plastics LNP Thermocomp MFK42AS PP (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP Thermocomp MFK42AS PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MFK42AS PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MFK42AS is a compound based on PP resin containing Glass Fiber, Mineral.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % @Temperature 23.0 °C, Time 86400 sec |
0.020 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.4 % | 5.4 % | Flexural Strain, 2 mm/min; ISO 178 |
| Elongation at Yield | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.00 GPa | 725 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 37.0 MPa | 5370 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 74.0 MPa | 10700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 51.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
28.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 116 µm/m-°C @Temperature 23.0 - 60.0 °C |
64.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ B700 X2 Polyamide 6 (Nylon 6)
- Zircar Zirconia ZYK-15 Zirconia Cloth Insulation
- Minelco FireCarb TEG-160 Expandable Graphite
- Silberline Tufflake® 3645
- Plenco 2535 Phenolic, Granular, Injection Molded
- Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf)
- Fainplast Compounds CTS 55/1 Flexible PVC, Extrusion Modified with Rubber
- Murtfeldt Murylat® SP Polyethylene Terephthalate
- Dow Corning XIAMETER® PMCPPMX-200 10CS Silicone Fluid
- Schmolz + Bickenbach Formadur® 2083 Superclean Plastic Mold Steel
Copyright © lookpolymers.com All Rights Reserved