Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Polyester (PBT), 30 wt.% glass Thermoplastic Polyesters are resistant to most organic solvents, weak acids and alkalis. They are not recommended with strong acids and alkalis or for prolonged use in hot water. Data provided by t.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ASTM D638 |
Shell Carilon® DP R1130 Polyketone, 30% Glass Fiber Reinforced
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP R1130 is a 30 percent glass fiber reinforced compound based on a developmental e.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527 |
LATI LAXTAR G/30 30% Glass Reinforced LCP
(discontinued **) Description: Laxtar products are liquid crystal polymers (LCP). They offer exceptional performance together with increasing cost-effectiveness. Due to the outstanding fluidity at high shear rates LC.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527 |
Solvay Specialty Polymers Ryton® R-7-120NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-7-120NA is an advanced glass/mineral filled polyphenylene sulfide compound developed to provide good weldline strength and low maintenance moldi.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527 |
Solvay Specialty Polymers Ryton® R-7-120BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-7-120BL is an advanced glass/mineral filled polyphenylene sulfide compound developed to provide good weldline strength and low maintenance molding using.. |
|||
Tensile Strength, Ultimate | 130 MPa @Temperature 1095 °C |
18900 psi @Temperature 2003 °F |
|
Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1, 2 |
Polyplastics FR-PET® CN9030 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose Information provided by PolyPlastics. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 260 SXF PBT-GF30 FR(17) 30% Glass Reinforced, Flame Retardant, High Flow |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 261 SF PBT-GF30 FR(17) 30% Glass Reinforced, Flame Retardant, High Flow |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 461 (PBT+PET)-GF30 30% Glass Reinforced |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 461 KL (PBT+PET)-GF30 30% Glass Reinforced, Heat Stabilized, UV Stabilized, Excellent Surface Properties |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | cond; ISO 527-1/-2 |
DSM EcoPaXX® Q-X07209 PA410-I-GF40 % Glass Reinforced, Impact Modified |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1013G15 1 NA PA6-GF15 15% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1013GH15 1 NA/BK37 PA6-GF15 15% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Tensile Strength, Ultimate | 130 MPa @Temperature 120 °C |
18900 psi @Temperature 248 °F |
ISO 527-1/-2 |
DSM Stanyl® TE200F8 PA46-GF40 40% Glass Reinforced, Heat Stabilized, for E&E applications |
|||
Tensile Strength, Ultimate | 130 MPa @Temperature 120 °C |
18900 psi @Temperature 248 °F |
ISO 527-1/-2 |
DSM Stanyl® TW272B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Dry) Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO R527 |
Arkema Group Orgalloy® RS 6030 Polyamide 6 Alloy 30% Glass Fiber reinforced Polyamide Alloy, Rigid grade, Nylon 6 basedMolding of Engineering PartsInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4300 G6 BKQ16 15007 PBT |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4406 G4 BKQ113 7110 20% Glass Filled PBT Ultradur B 4406 G4 BKQ113 7110 is an UL V0 injection molding, pigmented black, PBT grade with 20% glass fiber reinforcement. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Ultramid® A3EG3 15% Glass Filled PA66 (Dry) Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Ultramid® B3GM35 BKQ642 23220 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid B3GM35 BKQ642 23220 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 261 KL PBT-GF30 30% Glass Reinforced, Light Stabilized |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 264 SN PBT-GF30 FR(17) 30% Glass Reinforced, Flame Retardant |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ASTM D638 |
Chevron Phillips Ryton® R-7 02 Polyphenylene Sulfide Compound
(discontinued **) Black Polyphenylene Sulfide CompoundRyton® R-7 02 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compound wit.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1, 2 |
Polyplastics Duracon® CH-15 Acetal Co-polymer (POM), Conductive, CF reinforced, Wear resistance DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5 mm/min |
Arkema Group Orgalloy® RS 6030 Nylon 6 Alloy, 30% Glass Fiber (Conditioned) RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties.. |