Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet

Category Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabricated and formed, excellent resistance to molten chloride salts, and good resistance to gaseous sulfidation. Applications include a variety of fabricated component applications in the aerospace industry, commercial gas turbine engines for combustion cans, transition ducts and afterburner components.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.98 g/cc
0.324 lb/in³
at RT.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 945 MPa
137000 psi
130 MPa
<br>@Temperature 1095 °C
 18900 psi
<br>@Temperature 2003 °F
245 MPa
<br>@Temperature 980 °C
 35500 psi
<br>@Temperature 1800 °F
415 MPa
<br>@Temperature 870 °C
 60200 psi
<br>@Temperature 1600 °F
620 MPa
<br>@Temperature 760 °C
 89900 psi
<br>@Temperature 1400 °F
710 MPa
<br>@Temperature 650 °C
 103000 psi
<br>@Temperature 1200 °F
750 MPa
<br>@Temperature 540 °C
 109000 psi
<br>@Temperature 1000 °F
Tensile Strength, Yield 465 MPa
<br>@Strain 0.200 %
 67400 psi
<br>@Strain 0.200 %
64.0 MPa
<br>@Strain 0.200 %,<br> Temperature 1095 °C
 9280 psi
<br>@Strain 0.200 %,<br> Temperature 2003 °F
130 MPa
<br>@Strain 0.200 %,<br> Temperature 980 °C
 18900 psi
<br>@Strain 0.200 %,<br> Temperature 1800 °F
250 MPa
<br>@Strain 0.200 %,<br> Temperature 870 °C
 36300 psi
<br>@Strain 0.200 %,<br> Temperature 1600 °F
270 MPa
<br>@Strain 0.200 %,<br> Temperature 760 °C
 39200 psi
<br>@Strain 0.200 %,<br> Temperature 1400 °F
275 MPa
<br>@Strain 0.200 %,<br> Temperature 650 °C
 39900 psi
<br>@Strain 0.200 %,<br> Temperature 1200 °F
290 MPa
<br>@Strain 0.200 %,<br> Temperature 540 °C
 42100 psi
<br>@Strain 0.200 %,<br> Temperature 1000 °F
Elongation at Break 53 %
53 %
in 51 mm
32 %
<br>@Temperature 1095 °C
 32 %
<br>@Temperature 2003 °F
 in 51 mm
59 %
<br>@Temperature 650 °C
 59 %
<br>@Temperature 1200 °F
 in 51 mm
59 %
<br>@Temperature 980 °C
 59 %
<br>@Temperature 1800 °F
 in 51 mm
61 %
<br>@Temperature 540 °C
 61 %
<br>@Temperature 1000 °F
 in 51 mm
63 %
<br>@Temperature 760 °C
 63 %
<br>@Temperature 1400 °F
 in 51 mm
64 %
<br>@Temperature 870 °C
 64 %
<br>@Temperature 1600 °F
 in 51 mm
Modulus of Elasticity 232 GPa
33600 ksi
RT
153 GPa
<br>@Temperature 1000 °C
 22200 ksi
<br>@Temperature 1830 °F
161 GPa
<br>@Temperature 900 °C
 23400 ksi
<br>@Temperature 1650 °F
169 GPa
<br>@Temperature 800 °C
 24500 ksi
<br>@Temperature 1470 °F
176 GPa
<br>@Temperature 700 °C
 25500 ksi
<br>@Temperature 1290 °F
184 GPa
<br>@Temperature 600 °C
 26700 ksi
<br>@Temperature 1110 °F
193 GPa
<br>@Temperature 500 °C
 28000 ksi
<br>@Temperature 932 °F
201 GPa
<br>@Temperature 400 °C
 29200 ksi
<br>@Temperature 752 °F
209 GPa
<br>@Temperature 300 °C
 30300 ksi
<br>@Temperature 572 °F
217 GPa
<br>@Temperature 200 °C
 31500 ksi
<br>@Temperature 392 °F
225 GPa
<br>@Temperature 100 °C
 32600 ksi
<br>@Temperature 212 °F
Charpy Impact 194 J
143 ft-lb
solution annealed
Thermal Properties Metric English Comments
CTE, linear 11.9 µm/m-°C
<br>@Temperature 25.0 - 100 °C
 6.61 µin/in-°F
<br>@Temperature 77.0 - 212 °F
12.6 µm/m-°C
<br>@Temperature 25.0 - 200 °C
 7.00 µin/in-°F
<br>@Temperature 77.0 - 392 °F
13.2 µm/m-°C
<br>@Temperature 25.0 - 300 °C
 7.33 µin/in-°F
<br>@Temperature 77.0 - 572 °F
13.8 µm/m-°C
<br>@Temperature 25.0 - 400 °C
 7.67 µin/in-°F
<br>@Temperature 77.0 - 752 °F
14.5 µm/m-°C
<br>@Temperature 25.0 - 500 °C
 8.06 µin/in-°F
<br>@Temperature 77.0 - 932 °F
15.2 µm/m-°C
<br>@Temperature 25.0 - 600 °C
 8.44 µin/in-°F
<br>@Temperature 77.0 - 1110 °F
15.8 µm/m-°C
<br>@Temperature 25.0 - 700 °C
 8.78 µin/in-°F
<br>@Temperature 77.0 - 1290 °F
16.5 µm/m-°C
<br>@Temperature 25.0 - 800 °C
 9.17 µin/in-°F
<br>@Temperature 77.0 - 1470 °F
17.1 µm/m-°C
<br>@Temperature 25.0 - 800 °C
 9.50 µin/in-°F
<br>@Temperature 77.0 - 1470 °F
17.9 µm/m-°C
<br>@Temperature 25.0 - 1000 °C
 9.94 µin/in-°F
<br>@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.403 J/g-°C
0.0963 BTU/lb-°F
RT
0.423 J/g-°C
<br>@Temperature 100 °C
 0.101 BTU/lb-°F
<br>@Temperature 212 °F
0.444 J/g-°C
<br>@Temperature 200 °C
 0.106 BTU/lb-°F
<br>@Temperature 392 °F
0.465 J/g-°C
<br>@Temperature 300 °C
 0.111 BTU/lb-°F
<br>@Temperature 572 °F
0.486 J/g-°C
<br>@Temperature 400 °C
 0.116 BTU/lb-°F
<br>@Temperature 752 °F
0.502 J/g-°C
<br>@Temperature 500 °C
 0.120 BTU/lb-°F
<br>@Temperature 932 °F
0.523 J/g-°C
<br>@Temperature 600 °C
 0.125 BTU/lb-°F
<br>@Temperature 1110 °F
0.540 J/g-°C
<br>@Temperature 700 °C
 0.129 BTU/lb-°F
<br>@Temperature 1290 °F
0.557 J/g-°C
<br>@Temperature 800 °C
 0.133 BTU/lb-°F
<br>@Temperature 1470 °F
0.573 J/g-°C
<br>@Temperature 900 °C
 0.137 BTU/lb-°F
<br>@Temperature 1650 °F
0.590 J/g-°C
<br>@Temperature 1000 °C
 0.141 BTU/lb-°F
<br>@Temperature 1830 °F
Thermal Conductivity 10.4 W/m-K
72.2 BTU-in/hr-ft²-°F
RT
Electrical Properties Metric English Comments
Electrical Resistivity 0.000101 ohm-cm
0.000101 ohm-cm
RT
0.000103 ohm-cm
<br>@Temperature 100 °C
 0.000103 ohm-cm
<br>@Temperature 212 °F
0.000105 ohm-cm
<br>@Temperature 200 °C
 0.000105 ohm-cm
<br>@Temperature 392 °F
0.0001077 ohm-cm
<br>@Temperature 300 °C
 0.0001077 ohm-cm
<br>@Temperature 572 °F
0.0001105 ohm-cm
<br>@Temperature 400 °C
 0.0001105 ohm-cm
<br>@Temperature 752 °F
0.0001127 ohm-cm
<br>@Temperature 500 °C
 0.0001127 ohm-cm
<br>@Temperature 932 °F
0.0001148 ohm-cm
<br>@Temperature 600 °C
 0.0001148 ohm-cm
<br>@Temperature 1110 °F
0.0001164 ohm-cm
<br>@Temperature 700 °C
 0.0001164 ohm-cm
<br>@Temperature 1290 °F
0.0001175 ohm-cm
<br>@Temperature 800 °C
 0.0001175 ohm-cm
<br>@Temperature 1470 °F
0.0001183 ohm-cm
<br>@Temperature 900 °C
 0.0001183 ohm-cm
<br>@Temperature 1650 °F
0.0001191 ohm-cm
<br>@Temperature 1000 °C
 0.0001191 ohm-cm
<br>@Temperature 1830 °F