DSM Arnite® TV4 461 (PBT+PET)-GF30
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnite® TV4 461 (PBT+PET)-GF30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | Sim. To ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | Sim. To ISO 62 |
| Viscosity | 12500 cP @Shear Rate 100000 1/s, Temperature 270 °C |
12500 cP @Shear Rate 100000 1/s, Temperature 518 °F |
|
| 16000 cP @Shear Rate 100000 1/s, Temperature 250 °C |
16000 cP @Shear Rate 100000 1/s, Temperature 482 °F |
||
| 20000 cP @Shear Rate 100000 1/s, Temperature 230 °C |
20000 cP @Shear Rate 100000 1/s, Temperature 446 °F |
||
| 600000 cP @Shear Rate 1.00 1/s, Temperature 270 °C |
600000 cP @Shear Rate 1.00 1/s, Temperature 518 °F |
||
| 800000 cP @Shear Rate 1.00 1/s, Temperature 250 °C |
800000 cP @Shear Rate 1.00 1/s, Temperature 482 °F |
||
| 1.75e+6 cP @Shear Rate 1.00 1/s, Temperature 230 °C |
1.75e+6 cP @Shear Rate 1.00 1/s, Temperature 446 °F |
||
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0032 cm/cm | 0.0032 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527-1/-2 |
| Tensile Modulus | 9.90 GPa | 1440 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.1 @Frequency 100 Hz |
4.1 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0015 @Frequency 100 Hz |
0.0015 @Frequency 100 Hz |
IEC 60250 |
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 |
Users viewing this material also viewed the following:
- RedEye On Demand VeroBlack PolyJet™ FC870 for Rapid Prototyping
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- Chase Plastics CP Pryme® PC110GR Polycarbonate, 10% Glass Fiber Reinforced, Mold Release
- Polyram RamSter PF306G6 PBT, 30% Glass Fiber
- A. Schulman POLYBATCH™ Blue 4500GZ Concentrate Based in Low-Density Polyethylene
- Chicago Extruded Metals UNS C48200 Copper-Zinc-Tin Alloy
- ExxonMobil 100 Special Mobiltemp SHC Series
- Arkema Group Rilsan® Clear G380 Renew Polyamide
Copyright © lookpolymers.com All Rights Reserved