BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 1.4 %
1.4 %
24 hour; ISO Test
8.1 %
8.1 %
ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
23°C/50% R.H.; ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM Test
Tensile Strength at Break 130 MPa
18900 psi
0.2 in/min; ASTM Test
50.0 MPa

@Temperature 120 °C
7250 psi

@Temperature 248 °F
ASTM Test
50.0 MPa

@Temperature 120 °C
7250 psi

@Temperature 248 °F
ISO Data
60.0 MPa

@Temperature 80.0 °C
8700 psi

@Temperature 176 °F
ISO Data
60.0 MPa

@Temperature 80.0 °C
8700 psi

@Temperature 176 °F
ASTM Test
150 MPa

@Temperature -40.0 °C
21800 psi

@Temperature -40.0 °F
ASTM Test
150 MPa

@Temperature -40.0 °C
21800 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 130 MPa
18900 psi
5mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
3.0 %
3.0 %
0.2 in/min; ASTM Test
3.0 %

@Temperature -40.0 °C
3.0 %

@Temperature -40.0 °F
ASTM Test
3.0 %

@Temperature -40.0 °C
3.0 %

@Temperature -40.0 °F
ISO Data
10 %

@Temperature 120 °C
10 %

@Temperature 248 °F
ISO Data
10 %

@Temperature 120 °C
10 %

@Temperature 248 °F
ASTM Test
14 %

@Temperature 80.0 °C
14 %

@Temperature 176 °F
ASTM Test
14 %

@Temperature 80.0 °C
14 %

@Temperature 176 °F
ISO Data
Tensile Modulus 6.13 GPa
889 ksi
1mm/min; ISO 527
2.02 GPa

@Temperature 120 °C
293 ksi

@Temperature 248 °F
ISO Data
2.45 GPa

@Temperature 80.0 °C
355 ksi

@Temperature 176 °F
ISO Data
6.88 GPa

@Temperature -40.0 °C
998 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 160 MPa
23200 psi
ISO Data
Flexural Modulus 4.77 GPa
692 ksi
ISO Data
5.20 GPa
754 ksi
ASTM Test
Izod Impact, Notched 0.450 J/cm

@Thickness 3.17 mm
0.843 ft-lb/in

@Thickness 0.125 in
ASTM Test
Charpy Impact Unnotched 3.10 J/cm²
14.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 50.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
27.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 196 °C
385 °F
ISO 75
201 °C
394 °F
ASTM Test
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes