DSM EcoPaXX® Q-X07209 PA410-I-GF40
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | EcoPaXX® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM EcoPaXX® Q-X07209 PA410-I-GF40.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
% Glass Reinforced, Impact Modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.20 % | 1.20 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | cond; ISO 527-1/-2 |
| 180 MPa | 26100 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 4.0 % | 4.0 % | dry; ISO 527-1/-2 |
| 5.4 % | 5.4 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 8.20 GPa | 1190 ksi | cond; ISO 527-1/-2 |
| 11.0 GPa | 1600 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 190 MPa | 27600 psi | cond; ISO 178 |
| 270 MPa | 39200 psi | dry; ISO 178 | |
| Flexural Modulus | 8.10 GPa | 1170 ksi | cond; ISO 178 |
| 10.5 GPa | 1520 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | cond; IEC 60243-1 |
| 38.0 kV/mm | 965 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | cond; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Calculated Bio Based Carbon Content (%) | 67 | ASTM 6866 |
Users viewing this material also viewed the following:
- Albis Plastics PC/PET 361E Unfilled (discontinued **)
- Plenco 4100 Phenolic, Granular, Compression Molded (discontinued **)
- LG Chemical LUPOL HI5205 PP+MF20%, High Impact
- SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA 6/10 (Asia Pacific)
- Tra-Con Tra-Bond FS420 Flexible Plastic Adhesive
- ChevronTexaco ISO 320 Industrial Oil EP
- Chosun Refractories TCH-165Y Torpedo Castable
- Ascend Performance Materials Vydyne® R525H BK02 Nylon 66, 25% Glass Reinforced, Conditioned
- Ravago Manufacturing Americas Hylon® N2200 HL Nylon 6/6 (discontinued **)
Copyright © lookpolymers.com All Rights Reserved