Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 150 MPa | 21800 psi | Same value from ASTM and ISO tests; 5 mm/min. |
BASF Capron® GR20 20% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron GR20 is a 20% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aesthetics. It is also.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | Same value from ASTM and ISO tests; 5 mm/min. |
BASF Capron® GR20 HS 20% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron GR20 HS is a heat stabilized 20% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aest.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM data at 5 mm/min. |
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with.. |
|||
Tensile Strength, Ultimate | 150 - 160 MPa @Temperature 80.0 - 80.0 °C |
21800 - 23200 psi @Temperature 176 - 176 °F |
Average value: 155 MPa Grade Count:2 |
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® R-4 02 Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4 02 is a 40% fiberglass reinforced polyphenylene sulfide compound which provides outstanding chemical resistance and mechanical properties even at elev.. |
|||
Tensile Strength, Ultimate | >= 150 MPa | >= 21800 psi | |
Hybrid Plastics Fireban® Mark VI Resorcinolinic (PRF) The resin system produces a superiour fire resistant material.Information provided by Hybrid Plastics |
|||
Tensile Strength, Ultimate | >= 150 MPa | >= 21800 psi | |
Hybrid Plastics Fireban® Mark VII Resorcinolinic (PRF) The resin system produces a superiour fire resistant material.Information provided by Hybrid Plastics |
|||
Tensile Strength, Ultimate | >= 150 MPa | >= 21800 psi | |
Hybrid Plastics Fireban® Mark VI-IS Resorcinolinic (PRF) The resin system produces a superiour fire resistant material.Information provided by Hybrid Plastics |
|||
Tensile Strength, Ultimate | 150 MPa @Temperature 22.0 °C |
21800 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 1100 Unsaturated Polyester UP SMC 1100 is a special vinylester SMC for high strength applications. The reinforcement has been put to a level that combines mouldability with high strength and stiffness properties. The specific re.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | |
ICE Al2O3 99.8 Data provided by the manufacturer, International Ceramic Engineering. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ISO 527 |
Solvay Technyl® A 218 V35 Nylon 66, 35% Glass Fiber, EH50 Polyamides PA66, reinforced with 35% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V35 is used in all sectors of industry, offering an excellent combination between thermal an.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | |
Wieland 3005 Wilaform Silver Fine silver. Particularly suitable for minting or technical purposes.Applications: chains, coin/shape, laminar decoration, pipesDental |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | dry; ISO 527-1/-2 |
DSM Akulon® SG-KGS6 PA66-GF30 FR 30% Glass Reinforced, Halogen free and free of red phosphorous |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | dry; ISO 527-1/-2 |
DSM Akulon® Ultraflow K-FKGS6 /B PA6-GF30 FR(17) 30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ISO 527-1/-2 |
DSM Arnite® AV2 370 XL-T PET-GF35 35% Glass Reinforced, Low Outgassing, Thermal conductive material |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | dry; ISO 527-1/-2 |
DSM EcoPaXX® Q-PG6 PA410-I-GF30 % Glass Reinforced, Impact Modified |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | cond; ISO 527-1/-2 |
DSM Novamid® 1013G45 1 NA PA6-GF45 45% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | cond; ISO 527-1/-2 |
DSM Novamid® 1013GH45 1 NA/BK701 PA6-GF45 45% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Tensile Strength, Ultimate | 150 MPa @Temperature 120 °C |
21800 psi @Temperature 248 °F |
ISO 527-1/-2 |
DSM Stanyl® 46HF4550 PA46-GF50 50% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | cond; ISO 527-1/-2 |
DSM Stanyl® TW200B6 PA46-CF30 30% Carbon Reinforced, Heat Stabilized, Lubricated |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | |
China Tungsten STG10-15 PM Structural Parts Information provided by China Tungsten |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | |
China Tungsten STG60-15 PM Structural Parts Information provided by China Tungsten |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | 5mm/min; ISO 527 |
BASF Petra® 7030 GY6128 30% Glass Filled PET Petra 7030 GY6128 is a grey pigmented, high flow 30% glass fiber reinforced injection molding compound based on post-consumer and post-industrial recycled polyethylene terephthalate feedstock. It o.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4040 G10 High Speed BK15029 50% Glass Filled PBT/PET Ultradur B 4040 G10 High Speed BK15029 is a high flow, fast cycling with low warpage, 50% glass filled, injection molding PBT for industrial parts, rigid tough and dimensional stable applications. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM data at 5 mm/min. |
BASF Capron® 8333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G is a 33% glass reinforced nylon 6 modified compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness, and excel.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM data at 5 mm/min. |
BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G HI is a 33% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance .. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM data at 5 mm/min. |
BASF Capron® 8333G HI HS BK-102 Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G HI HS BK-102 is a 33% glass reinforced, impact modified polyamide 6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in c.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM D638 |
Solvay Specialty Polymers Ixef® 1501/0003 Polyarylamide, 30% Glass Fiber, at Equilibrium (65% RH)
(discontinu The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ISO 527 |
LATI LARTON G/50 50% Glass Fiber Filled Polyphenylene sulfide (PPS)
(discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Polyphenylene Sulfide, 40 wt.% glass Polyphenylene Sulfide provides excellent resistance to organic solvents (below 375°F). It is unaffected by strong alkalis or aqueous organic salt solutions. Data provided by the manufacturer, Owen.. |