DSM EcoPaXX® Q-PG6 PA410-I-GF30
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | EcoPaXX® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM EcoPaXX® Q-PG6 PA410-I-GF30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
% Glass Reinforced, Impact Modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.40 % | 1.40 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0067 cm/cm | 0.0067 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
| 150 MPa | 21800 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 4.5 % | 4.5 % | dry; ISO 527-1/-2 |
| 5.8 % | 5.8 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | cond; ISO 527-1/-2 |
| 8.00 GPa | 1160 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 160 MPa | 23200 psi | cond; ISO 178 |
| 220 MPa | 31900 psi | dry; ISO 178 | |
| Flexural Modulus | 5.80 GPa | 841 ksi | cond; ISO 178 |
| 7.50 GPa | 1090 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C | 30.6 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C | 36.1 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | dry; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | cond; IEC 60243-1 |
| 40.0 kV/mm | 1020 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | cond; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Calculated Bio Based Carbon Content (%) | 66 | ASTM 6866 |
Users viewing this material also viewed the following:
- ICO Polymers ICORENEâ„¢ 190-1327 LMDPE Rotational Molding Resin
- Karina E 360-06/719-IS-SD Blue PVC Compound
- Henkel Frekote B-15 Sealer Mold Sealer
- Techmer ES Statiblend® PA6 GF30 AS BK 30% Glass Filled
- XADC-Armoloy Armoloy® TDC Hard Chromium Coating
- ConocoPhillips SynXPA® HC-150 H Lubricant HC-150
- Braskem LH 0820/30 AF LLDPE Blown Film Extrusion Polyethylene
- A. Schulman ComAlloy Voloy® 686 Nylon 6/6, Glass Fiber/Bead Reinforced, Nylon 6/6 Alloy, Flame Retardant, UL