Solvay Technyl® A 218 V35 Nylon 66, 35% Glass Fiber, EH50
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 218 V35 Nylon 66, 35% Glass Fiber, EH50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamides PA66, reinforced with 35% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V35 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade in commonly used in the automotive industry of engine components, such as inlet manifolds, air ducts, engine cover, and various housing and liquid containers.This product is available in natural, black and grey.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183-A |
| Water Absorption | 0.75 % | 0.75 % | (Beginning Dry) 24 hours in water 23°C. ISO 62 |
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | ISO 527 |
| Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | ISO 527 |
| Flexural Yield Strength | 195 MPa | 28300 psi | ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ISO 178 |
| Izod Impact Resistance | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179/1EA-1993 |
| Charpy Impact, Notched | 1.85 J/cm² | 8.80 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 93 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 243-1 |
| Dissipation Factor | 0.11 @Frequency 1e+6 Hz |
0.11 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F |
Users viewing this material also viewed the following:
- Chevron Phillips 7109CLT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- DSM Akulon® K-FHGM35 (Dry) 40% Glass/Mineral Reinforced, Nylon 6 (North America) (discontinued **)
- Kinlead PP11 Printing Grade BOPP Plain Film (thickness: 30 µm)
- Mo-Sci Corporation GL-0176 Barium-Titanate Glass Spheres
- LATI Larpeek 50 PEEK
- Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes
- Borealis BB213CF Polypropylene Copolymer
- Terio Corporation TZOH-40 Zirconium Hydroxide
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Mistron Vapor Filler
- C.O.I.M. DIEXTER® G680 Polyol Polyester
Copyright © lookpolymers.com All Rights Reserved