DSM Stanyl® TW200B6 PA46-CF30

Category	Polymer , Thermoplastic , Nylon , Nylon 46
Manufacturer	DSM Engineering Plastics
Trade Name	Stanyl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DSM Stanyl® TW200B6 PA46-CF30.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

30% Carbon Reinforced, Heat Stabilized, Lubricated

Physical Properties	Metric	English	Comments
Density	1.28 g/cc	0.0462 lb/in³	dry; ISO 1183
Moisture Absorption	2.60 %	2.60 %	Sim. To ISO 62
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	150 MPa	21800 psi	cond; ISO 527-1/-2
	240 MPa	34800 psi	dry; ISO 527-1/-2
	95.0 MPa @Temperature 180 °C	13800 psi @Temperature 356 °F	ISO 527-1/-2
	105 MPa @Temperature 160 °C	15200 psi @Temperature 320 °F	ISO 527-1/-2
	125 MPa @Temperature 120 °C	18100 psi @Temperature 248 °F	ISO 527-1/-2
Elongation at Break	2.0 %	2.0 %	dry; ISO 527-1/-2
	4.0 %	4.0 %	cond; ISO 527-1/-2
	3.0 % @Temperature 120 °C	3.0 % @Temperature 248 °F	ISO 527-1/-2
	3.0 % @Temperature 160 °C	3.0 % @Temperature 320 °F	ISO 527-1/-2
	3.0 % @Temperature 180 °C	3.0 % @Temperature 356 °F	ISO 527-1/-2
Tensile Modulus	24.0 GPa	3480 ksi	dry; ISO 527-1/-2
	8.30 GPa @Temperature 180 °C	1200 ksi @Temperature 356 °F	ISO 527-1/-2
	8.80 GPa @Temperature 160 °C	1280 ksi @Temperature 320 °F	ISO 527-1/-2
	10.0 GPa @Temperature 120 °C	1450 ksi @Temperature 248 °F	ISO 527-1/-2
Flexural Modulus	9.20 GPa	1330 ksi	cond; ISO 178
	18.5 GPa	2680 ksi	dry; ISO 178
Fatigue Strength	60.0 MPa @# of Cycles 1.00e+7 , Temperature 140 °C	8700 psi @# of Cycles 1.00e+7 , Temperature 284 °F	R = 0.1, 8 Hz, dry
	67.0 MPa @# of Cycles 1.00e+6 , Temperature 140 °C	9720 psi @# of Cycles 1.00e+6 , Temperature 284 °F	R = 0.1, 8 Hz, dry
	77.0 MPa @# of Cycles 100000 , Temperature 140 °C	11200 psi @# of Cycles 100000 , Temperature 284 °F	R = 0.1, 8 Hz, dry
	87.0 MPa @# of Cycles 10000 , Temperature 140 °C	12600 psi @# of Cycles 10000 , Temperature 284 °F	R = 0.1, 8 Hz, dry
	100 MPa @# of Cycles 1000 , Temperature 140 °C	14500 psi @# of Cycles 1000 , Temperature 284 °F	R = 0.1, 8 Hz, dry
	115 MPa @# of Cycles 100 , Temperature 140 °C	16700 psi @# of Cycles 100 , Temperature 284 °F	R = 0.1, 8 Hz, dry
Izod Impact Resistance	0.650 J/cm² @Temperature -40.0 °C	3.09 ft-lb/in² @Temperature -40.0 °F	cond; ISO 180/1A
	0.650 J/cm² @Temperature -40.0 °C	3.09 ft-lb/in² @Temperature -40.0 °F	dry; ISO 180/1A
	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	dry; ISO 180/1A
	1.40 J/cm² @Temperature 23.0 °C	6.66 ft-lb/in² @Temperature 73.4 °F	cond; ISO 180/1A
Charpy Impact Unnotched	5.00 J/cm² @Temperature -30.0 °C	23.8 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eU
	5.00 J/cm² @Temperature -30.0 °C	23.8 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eU
	6.00 J/cm² @Temperature 23.0 °C	28.6 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eU
	7.50 J/cm² @Temperature 23.0 °C	35.7 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eU
Charpy Impact, Notched	0.650 J/cm² @Temperature -30.0 °C	3.09 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eA
	0.650 J/cm² @Temperature -30.0 °C	3.09 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eA
	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA
	1.40 J/cm² @Temperature 23.0 °C	6.66 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	8.00 µm/m-°C	4.44 µin/in-°F	dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow	34.0 µm/m-°C	18.9 µin/in-°F	dry; ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	290 °C	554 °F	dry; ISO 75-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	100 ohm-cm	100 ohm-cm	dry; IEC 60093