Polymer Property : Flexural Yield Strength = 108 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	108 MPa	15700 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS High heat PC/ABS blend offering high modulus / low CTE and good practical impact
Flexural Yield Strength	108 MPa	15700 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS (Asia Pacific) High heat PC/ABS blend offering high modulus / low CTE and good practical impact
Flexural Yield Strength	108 MPa	15700 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS (Europe-Africa-Middle East) High heat PC/ABS blend offering high modulus / low CTE and good practical impactThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength	108 MPa	15700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® DMX2415 PC Lexan* DMX2415 is a polycarbonate resin with improved scratch resistance. Lexan* DMX2415 is available in transparent, translucent, and opaque colors.This data was supplied by SABIC-IP for the Americ..
Flexural Yield Strength	108 MPa	15700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® DMX2415 PC (Asia Pacific) Lexan* DMX2415 is a polycarbonate resin with improved scratch resistance. Lexan* DMX2415 is available in transparent, translucent, and opaque colors.This data was supplied by SABIC-IP for the Asia P..
Flexural Yield Strength	108 MPa	15700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® DMX3415 PC Copolymer Lexan* DMX3415 is a co-polycarbonate resin with improved scratch resistance, high purity and optical quality.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	108 MPa	15700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm, opaque polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	108 MPa	15700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer (Europe-Africa-Middle East) Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm, opaque polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea..
Flexural Yield Strength	108 MPa	15700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	108 MPa	15700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer (Asia Pacific) This product will be phased out per January 2015 -- Lexan* DMX1435 is a UV stabilized standard flow polycarbonate copolymer resin with improved scratch resistance.
Flexural Yield Strength	108 - 150 MPa	15700 - 21800 psi	Average value: 128 MPa Grade Count:5
Overview of materials for Ethylene Vinyl Alcohol (EVOH) This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Alcohol". Each property range of values reported is minimum and maximum values of appropr..
Flexural Yield Strength	108 MPa	15700 psi	Bending Strength; ASTM D790
EVALCA EVAL® LC-H101BD Ethylene Vinyl Alcohol Copolymer Resin (discontinued **) 38 mol % Ethylene.Data provided by EVALCA. Applications: Blown film. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of th..
Flexural Yield Strength	108 MPa @Thickness 6.40 mm	15600 psi @Thickness 0.252 in	2.8mm/min; ASTM D790
LG Chemical LUMID GN1001AF PA6, Halogen Free Flame Retardant Feature: Injection Molding, PA6, Halogen Free Flame RetardantApplication: Electrical & Electronic (Switch)CAS No. 25038-54-4 and 37640-57-6Information provided by LG Chemical
Flexural Yield Strength	108 MPa @Thickness 3.20 mm	15600 psi @Thickness 0.126 in	2.8mm/min; ASTM D790
LG Chemical LUMID GP1100A(W) PA6, Low Viscosity Feature: Injection Molding, PA6, Low ViscosityApplication: Industrial Material, Sport PartsCAS No. 25038-54-4Information provided by LG Chemical
Flexural Yield Strength	108 MPa @Thickness 3.20 mm	15600 psi @Thickness 0.126 in	2.8mm/min; ASTM D790
LG Chemical LUMID GP1200A(W) PA6, Medium Viscosity Feature: Injection Molding, PA6, Medium ViscosityApplication: Industrial Material, Sport PartsCAS No. 25038-54-4Information provided by LG Chemical
Flexural Yield Strength	108 MPa @Thickness 3.20 mm	15600 psi @Thickness 0.126 in	1.3mm/min; ASTM D790
LG Chemical LupoxÂ® GP2076F PBT+GF7% Description: Injection Molding, PBT+GF7%, Flame Retardant Application: IT/OA, E&E (Connector)CAS No. 68928-70-1, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chemical
Flexural Yield Strength	108 MPa @Thickness 3.20 mm	15600 psi @Thickness 0.126 in	15mm/min; ASTM D790
LG Chemical 82TR SAN, High Transparency, Heat Resistance, Chemical Resistance Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Refrigerator Sleeves, MiscellaneousCAS No. 9003-54-7Information provided by LG Chemical
Flexural Yield Strength	108 MPa @Thickness 3.20 mm	15600 psi @Thickness 0.126 in	10mm/min; ASTM D790
LG Chemical LUPOY GN5151RF PC/ABS Mineral Filler Description: Injection Molding, PC/ABS Mineral Filler, General Purpose, High Stiffness, Halogen Free Flame RetardantApplication: E&E (Housing), IT/OA (Notebook PC Housing)CAS: 103598-77-2, 9003-56-9..
Flexural Yield Strength	108 MPa	15700 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL ZWM2411 PPE+PS (Asia Pacific) Modified PPO*, 30% mineral filled product, V-1@1.5mm, HDT 125degC, low warpage product, BK color only
Flexural Yield Strength	108 MPa	15600 psi	ASTM D790
Samyang TramidÂ® 210 Polyamide, General Purpose Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210 is a general purpose grade.Applications:Automotive gear level housingConnecto..
Flexural Yield Strength	108 MPa	15600 psi	ASTM D790
Samyang TrirexÂ® SF3200GNH20 Polycarbonate, Reinforced Non Halogen for Printers PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.SF3200GNH20 is a reinforced, non-halogen grade for Printers.Applications: Office Machi..
Flexural Yield Strength	108 MPa	15700 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp ZWM2411 PPE+PS (Asia Pacific) Modified PPO*, 30% mineral filled product, V-1@1.5mm, HDT 125degC, low warpage product, BK color onlyThis data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Yield Strength	108 MPa	15700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp ZF0041XC PPE+PS (Europe-Africa-Middle East) LNP* THERMOCOMP* ZF0041XC is a compound based on PPE+PS Blend resin containing Glass Fiber and Flame retardant. Added features include Flame Retardant.This data was supplied by SABIC-IP for the Euro..
Flexural Yield Strength	108 MPa	15700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6 Noryl GTX* GTX675 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to a..
Flexural Yield Strength	108 MPa	15600 psi	ASTM D790
PlastxWorld CEVIAN® S1210 PC/ABS alloy Glass fiber reinforced PC/ABS alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Flexural Yield Strength	108 MPa	15700 psi	ASTM D790
Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, Dry As Molded Neat resin, for film or extrusion.Information provided by Cresset Powers Ltd.
Flexural Yield Strength	108 MPa @Thickness 6.40 mm	15600 psi @Thickness 0.252 in	5 mm/min; ASTM D790
Bhansali Engineering Santron IMS 2007LF SAN Resin High Rigidity Clear SANInformation provided by Bhansali
Flexural Yield Strength	108 MPa	15700 psi	ASTM D790
Toyobo T-751 Nylon, Painting Grade Key Feature: Glass fiber and mineral reinforced, high heat distortion and impact gradesInformation provided by Toyobo Co., Ltd
Flexural Yield Strength	108 MPa	15600 psi	ASTM D790
PlastxWorld CEVIAN® A5622 10% GF PA/ABS Alloy, DAM Property data is for dry as molded (DAM) samples.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.