- Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, Dry As Molded
Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, Dry As Molded
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Cresset Powers, Ltd |
| Trade Name | Cress-Alon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, Dry As Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Neat resin, for film or extrusion.Information provided by Cresset Powers Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 - 1.14 g/cc | 0.0405 - 0.0412 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | circa |
| Viscosity Measurement | 2.95 - 3.05 | 2.95 - 3.05 | Relative Viscosity |
| Melt Flow | 17.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
17.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
| Elongation at Yield | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Yield Strength | 108 MPa | 15700 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 224 °C | 435 °F | ASTM DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | <= 0.10 % | <= 0.10 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Extractables, wt% | <0.5 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® ES-40GF/000 Polyethersulfone - 40% Glass Fiber Reinforced (discontinued **)
- 3M Dyneon™ TFM™ 4215 Modified PTFE, 25% Electrocarbon Filled (discontinued **)
- M. Holland Company CP501 Polypropylene Impact Copolymer
- MarkeTech Lanthanum Aluminum Oxide (LaAlO3) Single Crystal Substrate
- Lubrizol Advanced Materials PEARLTHANE® 91T85 Thermoplastic Polyurethane Elastomer
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR N220 (ISAF) Filler
- Eurotec® Tecomid® NB40 NL IL PA 6 impact modified
- 3M Scotchkote™ 2400 Pipe Renewal Liner
- A. Schulman ComAlloy Hiloy® 446 Glass/Mineral Reinforced, PET Alloy
- LATI Latiohm 52/11-10 PD02 PP Homopolymer
Copyright © lookpolymers.com All Rights Reserved