BASF Novolen® 2248 TC Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Novolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Novolen® 2248 TC Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nucleated grade with antistatic agent for injection moldings.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 65 g/10 min @Load 2.16 kg, Temperature 230 °C |
65 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| Tensile Modulus | 1.55 GPa | 225 ksi | |
| Charpy Impact Unnotched | 16.0 J/cm² | 76.1 ft-lb/in² | |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | |
| 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 163 °C | 325 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | |
| Vicat Softening Point | 83.0 °C | 181 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | |
| Dielectric Constant | 2.3 @Frequency 1e+6 Hz |
2.3 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 140 kV/mm | 3560 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
|
| 0.00081 @Frequency 100 Hz |
0.00081 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Techmer ES Elastoblend® PA6 GF15 IM1 15% Glass Filled
- SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Asia Pacific)
- Sax Polymers SAXATEC 4307 Acrylonitrile Styrene Acrylate
- A. Schulman POLYBATCH™ Blue 40460/4 Concentrate Based In LLDPE
- Wellman Wellamid® GF60-66/6 XE-NBK1 60% Glass Fiber Reinforced, Engineering Grade Nylon 66/6
- A. Schulman POLYBATCH™ FSU-105-E Concentrate Based In LDPE
- BASF Pluracol® P710R Specialty Polyol
- Ceradyne Thermo-Sil® Isomolded™ Fused Silica
- A. Schulman FORMION™ FI 389 Ionomer
- Huntsman Tactix 138 Epoxy
Copyright © lookpolymers.com All Rights Reserved