- Aclo Accutech Polypropylene Homopolymer HP0336C30L1 Calcium Reinforced
Aclo Accutech Polypropylene Homopolymer HP0336C30L1 Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336C30L1 Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 29.1 % | 29.1 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 86 | 86 | ASTM D785 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 45 % | 45 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.900 GPa | 275.5 ksi | ASTM D638 |
| Flexural Strength | 36.0 MPa | 5220 psi | ASTM D790 |
| Flexural Modulus | 2.099 GPa | 304.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.470 J/cm | 0.880 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S EF 50A-3S1965 Thermoplastic Elastomer (TPE)
- Palm Labs Adhesives Turbo Fuse Series 150 (500 Viscosity) Rapid Bonding Adhesive
- SABIC Innovative Plastics Lexan® 925 PC
- Lubriplate SYN SYN-1602 PAO-Based Multi-Purpose Grease
- Teknor Apex APEX® SRP 2700A Polyvinyl Chloride, Rigid
- SABIC Innovative Plastics LNP Thermocomp GX05053 PSU (Europe-Africa-Middle East)
- Hexcel® HexForce™ XLS9103 Carbon/Wire Fabric
- A. Schulman POLYBATCH™ Orange 1770E Concentrate Based In Polyethylene
- Arkema Group Rilsan® AESN Y T6L Nylon 12, MoS2 Filled (Conditioned)
- Haynes Hastelloy® G-30® alloy, 19.1 mm thick plate
Copyright © lookpolymers.com All Rights Reserved