SABIC Innovative Plastics LNP THERMOCOMP WH0450E PBT

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP THERMOCOMP WH0450E PBT.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Thermocomp* WH0450E is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.

Physical Properties	Metric	English	Comments
Density	4.50 g/cc	0.163 lb/inÂ³	ASTM D792
	4.50 g/cc	0.163 lb/inÂ³	ISO 1183
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0080 cm/cm @Time 86400 sec	0.0080 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
	33.0 MPa	4790 psi	ISO 527
Tensile Strength, Yield	29.0 MPa	4210 psi	ISO 527
	30.0 MPa	4350 psi	ASTM D638
Elongation at Break	0.30 %	0.30 %	ASTM D638
	0.40 %	0.40 %	ISO 527
Elongation at Yield	0.30 %	0.30 %	ASTM D638
	0.30 %	0.30 %	ISO 527
Tensile Modulus	9.64 GPa	1400 ksi	1 mm/min; ISO 527
	14.39 GPa	2087 ksi	50 mm/min; ASTM D638
Flexural Strength	54.0 MPa	7830 psi	ISO 178
	55.0 MPa	7980 psi	ASTM D790
Flexural Modulus	11.48 GPa	1665 ksi	ISO 178
	11.7 GPa	1700 ksi	ASTM D790
Izod Impact, Notched	0.320 J/cm	0.599 ft-lb/in	ASTM D256
Izod Impact, Unnotched	1.08 J/cm	2.02 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	5.00 kJ/mÂ²	2.38 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	9.00 kJ/mÂ²	4.28 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	4.00 J	2.95 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	173 Â°C	343 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	182 Â°C @Thickness 3.20 mm	360 Â°F @Thickness 0.126 in	unannealed; ASTM D648