BASF Novolen® 3248 RC Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Novolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Novolen® 3248 RC Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Grade containing nucleating and antistatic agents for injection molded parts.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 31 g/10 min @Load 2.16 kg, Temperature 230 °C |
31 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 11 % | 11 % | |
| Tensile Modulus | 1.10 GPa | 160 ksi | |
| Charpy Impact Unnotched | 20.0 J/cm² | 95.2 ft-lb/in² | |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | |
| 0.150 J/cm² @Temperature -30.0 °C |
0.714 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 185 µm/m-°C @Temperature 20.0 °C |
103 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 150 °C | 302 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | |
| Vicat Softening Point | 72.0 °C | 162 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | |
| Dielectric Constant | 2.3 @Frequency 1e+6 Hz |
2.3 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 140 kV/mm | 3560 kV/in | |
| Dissipation Factor | 0.00081 @Frequency 100 Hz |
0.00081 @Frequency 100 Hz |
|
| 0.0020 @Frequency 1e+6 Hz |
0.0020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC (Asia Pacific)
- Solvay TECHNYL® C 246 V 30 PA6, 30% glass fiber, DRY
- Shamrock Technologies NanoFLON® P 63B Thermoplastic Grade PTFE Additive
- SABIC Innovative Plastics LNP STAT-KON EX99689C PEI
- SABIC Innovative Plastics LNP VERTON MV008S PP
- SABIC Innovative Plastics LNP THERMOCOMP DB0049F PC
- Tipco Tipcolite® THD 111 Phenolic Compound, Short Glass Fibers & Minerals, Medium -Soft Flow & High Strength
- A. Schulman POLYBLAK™ 4651SF Universal Black Color Concentrate, 50% Carbon Black in EVA
- Adell RR-16 Copolymer Polypropylene, 30% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved