Polymer Property : Tensile Strength, Yield = 4350 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	30.0 MPa	4350 psi	Type I, 51 mm/min; ASTM D638
PolyOne Maxxam™ PPH-20C Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Tensile Strength, Yield	30.0 - 40.0 MPa	4350 - 5800 psi	Injection and Compression; ISO 527
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi..
Tensile Strength, Yield	30.0 - 130 MPa	4350 - 18900 psi	Average value: 77.9 MPa Grade Count:91
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an..
Tensile Strength, Yield	30.0 - 70.0 MPa	4350 - 10200 psi	Average value: 47.9 MPa Grade Count:34
Overview of materials for Acetal Homopolymer, Unreinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced, Impact Grade". Each property range of values reported is minimum and m..
Tensile Strength, Yield	30.0 MPa @Temperature 23.0 °C	4350 psi @Temperature 73.4 °F	50 mm/min; ASTM D638
Solvay Specialty Polymers Halar® 513LC Polyethylene, Chlorotrifluoroethylene (ECTFE) (Unverified Data**)& Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield	30.0 MPa	4350 psi	Type 1 @ 2 in/min; ASTM D638
Chevron Phillips K-Resin® BK12 Styrene-Butadiene Copolymer, Injection Molding Grade (discontinued **) Styrene-Butadiene CopolymerCustomer Benefits: BK12 is an SBC consisting of KR01 grade with a mold release added for easier processing. BK12 molded parts give excellent detail on fast production cyc..
Tensile Strength, Yield	30.0 - 103 MPa	4350 - 14900 psi	Average value: 72.4 MPa Grade Count:24
Overview of materials for Nylon 6, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are includ..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
FiberfilÂ® PP-62/MI/25 Polypropylene Copolymer, 25% Mica Reinforced Information provided by FIBERFIL Engineered Plastics
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527
Styrolution PS 416N HIPS Styrolution PS 416N is medium impact polystyrene with very good flow properties. It has a high rigidity whilst displaying a very good surface gloss.Very good flow propertiesHigh rigidityVery good su..
Tensile Strength, Yield	30.0 MPa	4350 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MX95318 PP LNP* THERMOCOMP* MX95318 is a compound based on Polypropylene containing Proprietary Filler(s).
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
A. Schulman POLYFORT™ PP 2268UX Heat Resistant Polypropylene DescriptionPolyfort® PP 2268UX is a UV stabilized, extra high flow unique high modulus, heat resistant polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527-2
Total PPH 7089 Polypropylene Homopolymer, Fiber Polypropylene PPH 7089 is a narrow molecular weight distribution homopolymer polypropylene, with anti-gas fading stabilization.Polypropylene PPH 7089 is intended for the extrusion of fibers with the..
Tensile Strength, Yield	30.0 MPa	4350 psi	GB/1040
Zhejiang Juner JEPPB006 High Glossy PP Applications: Electric Rice CookerInformation provided by Zhejiang Juner New Materials Co, Ltd.
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass) DescriptionPolyflam® RPP 1058 is a general purpose homopolymer polypropylene flame retardant with a UL-V2 flammability rating and 105°C temperature index at 0.030 in.Information provided by A. Sch..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1068-32 Black40% Mineral Filled Polypropylene DescriptionPolyfort® FPP 1068-32 Black is a 40% mineral filled polypropylene designed for use when improved heat resistance, dimensional stability and high stiffness is needed. ApplicationApplicati..
Tensile Strength, Yield	30.0 MPa	4350 psi
TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 2.0 PHR MBTS MILLATHANE E34 is a high performance polyether polyurethane rubber for applications requiring: high abrasion resistance, low temperature flexibility, ozone resistance, oil and fuel resistance, outst..
Tensile Strength, Yield	30.0 MPa	4350 psi	dry; ISO 527
Ter Hell Plastic K-Resin KRE 9902 Butadiene-Styrene Copolymer Description: Butadiene-Styrene Copolymer Compound, good transparency with impact strength and stiffness well-balanced.Application: For all kinds of injection molded parts.Information provided by T..
Tensile Strength, Yield	30.0 MPa	4350 psi	2 in/min, Type IV bar; ASTM D-638
Chevron Phillips Marlex® 9514H Polyethylene; HDPE High density polyethylene. This gas phase, high molecular weight hexene copolymer is tailored for lightweight blow molded applications that: Require excellent stiffness to ESCR ratioRequire good m..
Tensile Strength, Yield	30.0 MPa @Temperature 200 °C	4350 psi @Temperature 392 °F	ISO 527-1/-2
DSM Stanyl® TW341-J PA46 Heat Stabilized, Lubricated
Tensile Strength, Yield	30.0 MPa	4350 psi
EMS-Grivory Grivory® L 25 W 20 Y PA12-I Product Description: Grilamid L 25 W 20 Y black 9992 is a semiflexible plasticized, medium viscosity, extrusion grade of Polyamide 12 (PA12). Grilamid L 25 W 20 Y black 9992 is impact modified, heat..
Tensile Strength, Yield	30.0 MPa	4350 psi
EMS-Grivory Grivory® L 25 W 20 PA12 Product Description: Grilamid L 25 W 20 is a semi-flexible plasticized high viscosity extrusion grade of Polyamide 12 (PA12). Grilamid L 25 W 20 is UV and heat stabilized. The main features of Grila..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Braskem RP 347 Injection Molding Polypropylene Description: RP 347 is a medium melt flow rate random copolymer designed for injection moulding. This product offers excellent transparency and gloss, very good stiffness/impact strength balance, ex..
Tensile Strength, Yield	30.0 MPa @Temperature 80.0 °C	4350 psi @Temperature 176 °F	ISO Data
BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique ..
Tensile Strength, Yield	30.0 MPa	4350 psi	50 mm/min
Arkema Group Rilsan® BECN P20 TL Nylon 11 (Conditioned) ISO data provided by the manufacturer, Arkema.
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
NOVA Chemicals Novapol® HB-W558-A HDPE Extrusion Resin (discontinued **) Molded Plaque Properties. Features: High molecular weight, excellent impact strength, high rigidity, easy processing.Applications: large part blow molding, large oil drums.Data provided by the manu..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Ineos Nova Zylar® 535 Clear Impact Modified Acrylic Copolymer (discontinued **) Features: High clarity, strength and toughnessStyrenic processing advantagesExcellent property retention after ETO and gamma sterilizationAnti-stat packageEnhanced mold releaseUL 94HB @ 1.5 mm for a..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass) DescriptionPolyflam® RPP 1058 is a general purpose homopolymer polypropylene flame retardant with a UL-V2 flammability rating and 105°C temperature index at 0.030 in.Information provided by A. Sch..
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527
Polyram RamSter PF801 PBT, High Impact Modified High impact modified PBT for injection molding applications.Information provided by Polyram.
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM-D638
Braskem BS600 HDPE Blow Molding Polyethylene Copolymer BS600 resin is a high-density polyethylene (HDPE), bimodal copolymer offering an outstanding combination of impact resistance and environmental stress crack resistance (ESCR). It is thus recommended..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM-D638
Braskem CP 404XP HECO Polypropylene Heterophasic Copolymer CP 404XP is a medium melt flow rate heterophasic copolymer with suitable additives to produce caps and closures for carbonated beverages. This product exhibits high stiffness and impact strength bal..