Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 77.0 MPa | 11200 psi | ISO 527-2 |
PolyOne Trilliant™ HC THC-02 1200 IL Natural Polyamide 66 (Nylon 66) The Trilliant® HC specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ah.. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer (Asia Pacific) This product will be phased out per January 2015 -- Lexan* DMX1214 resin is an improved flow, transparent copolycarbonate resin with improved scratch resistance. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer (Europe-Africa-Middle East) This product will be phased out per January 2015 -- Lexan* DMX1214 resin is an improved flow, transparent copolycarbonate resin with improved scratch resistance. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | |
Radici Radilon® S RV150 (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FST3403 PC Copolymer (Asia Pacific) Lexan* FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior .. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer XHT4141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer (Asia Pacific) XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. It is available in a range of opaque and limited transparent colors. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | ASTM D638 |
SABIC Innovative Plastics LNP COLORCOMP JX91550 PES LNP COLORCOMP* JX91550 is an unfilled Polyethersulfone. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | ASTM D638 |
SABIC Innovative Plastics LNP COLORCOMP JX91550 PES (Asia Pacific) LNP COLORCOMP* JX91550 is a compound based on Polyethersulfone resin containing Unfilled Custom Color. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL32P PC LNP* LUBRICOMP* DFL32P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated, Exceptional Processing. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | ISO 527-2 |
PolyOne Nymax™ 1200 IL Natural Polyamide 66 (Nylon 66) The Nymax® 1200 IL is an internally lubricated, unfilled nylon 6/6 designed for exceptional processing and mold release. This grade is intended primarily for injection molded applications where a g.. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer Lexan* DMX1214 resin is an improved flow, transparent copolycarbonate resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer (Asia Pacific) XHT4141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer (Europe-Africa-Middle East) XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. It is available in a range of opaque and limited transparent colors. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 10%/min. ASTM D638 |
EVALCA EVAL® LC-F101BZ Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **) 32 mol % Ethylene.Data provided by EVALCA. Applications: Blown film, cast film, melt phase forming, blow molding, profile coextrusion. EVOH is used in packaging applications because of its outstan.. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 50 mm/min; ASTM D638 |
LG Chemical 92HR SAN Resin Heat and chemical resistance, Good mechanical properties, Excellent processability, Superior transparency, Good dimensional stability, Applications include automobile battery cases, water meter case.. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL TN300 PPE+PS PPE+PS. Transparent. High heat. Color Limited. Injection molding. Laser-Transmission welding applications. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP LL002 PEEK LNP* LUBRICOMP* LL002 is a compound based on Polyetheretherketone containing 10% PTFE. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP LX00430 PEEK LNP* LUBRICOMP* LX00430 is a compound based on Pelyetheretherketone containing Proprietary Fillers. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP WFB62 PBT LNP* THERMOCOMP* WFB62 is a compound based on PBT resin containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Low Warpage. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH6020 PPE+HIPS Noryl NH6020 resin is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 .. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH6020 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH6020 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 mm an.. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp OF003A PPS (Asia Pacific) LNP* Thermocomp* OF003A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | |
Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix HexPly® M42 is a high performance, self extinguishing, self adhesive, tough epoxy matrix for use in primary aerospace sandwich structures. It exhibits very high impact resistance and damage toleran.. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | 50 mm/min; ISO 527 |
Chi Mei Kibisan® PN-127 SAN Heat Resistant |
|||
Tensile Strength, Yield | 77.0 MPa @Temperature 23.0 °C |
11200 psi @Temperature 73.4 °F |
EN ISO 527 |
Ensinger TECASINT 1061 Polyimide, 15% Graphite, 10% PTFE Filled (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | ASTM D638 |
E-Polymers TEKAMID® TB120L NCR , High Crystallinity PA6, DAM Precise injection, high crystallinityInformation provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 25WSP Nylon 66, Conditioned (2.5% Moisture) Vydyne® 25WSP is a black, weather resistant injection molding grade Nylon 66 resin. These resins offer a well-balanced combination of engineering properties characterized by high strength, rigidity.. |
|||
Tensile Strength, Yield | 77.2 MPa | 11200 psi | ASTM D638 |
Asahi Kasei Thermylene® P-25FG-0100 25% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Tensile Strength, Yield | 77.0 MPa | 11200 psi | ISO 527 |
Ascend Performance Materials Vydyne® 22WSP Nylon 66, Weather Resistant, Conditioned Vydyne® 25WSP is a black, weather resistant injection molding grade Nylon 66 resin. These resins offer a well-balanced combination of engineering properties characterized by high strength, rigidity.. |