Ascend Performance Materials Vydyne® 25WSP Nylon 66, Conditioned (2.5% Moisture)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 25WSP Nylon 66, Conditioned (2.5% Moisture).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 25WSP is a black, weather resistant injection molding grade Nylon 66 resin. These resins offer a well-balanced combination of engineering properties characterized by high strength, rigidity, good toughness, high melt point, good surface lubricity and abrasion resistance. Vydyne 25WSP maintains the chemical resistance typical of nylon to many chemicals, solvents, gasoline, and machine and motor oils. Weather resistance is obtained by incorporating finely divided, well dispersed carbon black particles in the nylon matrix. While the presence of carbon black usually increases brittleness, these resins have been formulated to minimize loss of ductility properties such as elongation and Izod impact strength. As a result, parts molded from 25WSP frequently exhibit higher ductility and practical toughness compared with other black, weather resistant, non-impact modified Nylon 66 molded parts. Vydyne 25WSP resins are internally and externally lubricated for improved machine feed and exceptional mold release. Vydyne 25WSP is intended for use in high-productivity applications. In many applications, the molding cycle can be reduced because molded parts may be removed from the cavity at higher temperatures. In difficult molds where parts have a tendency to stick in the cavity, Vydyne 25WSP can reduce or eliminate the need for mold release sprays. Critical molded part dimensions should be checked against specifications before implementing shorter molding cycles on a routine production basis. Typical Applications/End Uses. Lubricated for machine feed and mold release, Vydyne 25WSP provides very good flow and easy moldability. Typical applications include cable ties/ tie straps, where its combination of easy flow, good ductility, and high tensile strength is particularly attractive, and a wide variety of electrical/electronic and miscellaneous applications requiring weather resistance.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ISO 1183
Water Absorption 1.2 %

@Time 86400 sec
1.2 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.4 %
2.4 %
50% RH; ISO 62
Linear Mold Shrinkage 0.014 cm/cm

@Thickness 2.00 mm
0.014 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Thickness 2.00 mm
0.016 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 77.0 MPa
11200 psi
ISO 527-2
Elongation at Break 60 %
60 %
ISO 527-2
Elongation at Yield 25 %
25 %
ISO 527-2
Tensile Modulus 1.55 GPa
225 ksi
ISO 527-2
Flexural Strength 22.0 MPa
3190 psi
ISO 178
Flexural Modulus 1.40 GPa
203 ksi
ISO 178