SABIC Innovative Plastics LNP LUBRICOMP LL002 PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP LL002 PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* LL002 is a compound based on Polyetheretherketone containing 10% PTFE. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
| 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 |
| 77.0 MPa | 11200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 17.8 % | 17.8 % | 5 mm/min; ISO 527 |
| 52 % | 52 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.3 % | 5.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.28 GPa | 476 ksi | 1 mm/min; ISO 527 |
| 3.33 GPa | 483 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| Flexural Modulus | 3.07 GPa | 445 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.12 GPa | 453 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.840 J/cm | 1.57 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 29.9 J/cm | 56.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 158 kJ/m² | 75.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.39 | 0.39 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.35 | 0.35 | ASTM D3702 Modified |
| K (wear) Factor | 42.3 x 10-8 mm³/N-M | 21.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 166 °C @Thickness 3.20 mm |
331 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 7781 E-Glass Reinforced
- Michelman® Michem® Coat 218Cl4AF Corrosion inhibitor coating
- Techmer ES Elastoblend® PA6/6 GF15 IM HS L 15% Glass Filled
- Styron MAGNUMâ„¢ 1250 BG Acrylonitrile Butadiene Styrene (ABS) Resin
- Borealis Borcoat™ HE3453 Natural High Density Polyethylene for Steel Pipe Coating
- PlastxWorld CEVIAN®-N GRSJ3 30% GF SAN resin
- DuPont Elvanol® 70-03 Polyvinyl Alcohol Fully Hydrolyzed General Purpose Grade
- DuPont Vamac® DP HVA-2 Coagent Test Compound
- BASF Ethyl Chloroformate
- Sinotek Materials Soft Graphite Ring
Copyright © lookpolymers.com All Rights Reserved