Polymer Property : Tensile Strength, Yield = 10300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	71.0 MPa	10300 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
Tensile Strength, Yield	71.0 MPa	10300 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific) LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	71.0 MPa	10300 psi	ASTM D638
Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, at 50% RH (disc AMODEL AP-9240 NL resin is a 40% mineral-filled, impact-modified polyphthalamide (PPA). It was designed to provide a smooth molded surface suitable for many decorative applications. This resin offer..
Tensile Strength, Yield	71.0 MPa @Temperature 23.0 °C	10300 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Delrin® 100TL NC010 Acetal Homopolymer (Unverified Data**) Delrin® 100TL NC010 is a high viscosity acetal homopolymer with 1.5% Teflon® PTFE Micropowder.Information provided by DuPont Performance Polymers
Tensile Strength, Yield	71.0 MPa @Temperature 23.0 °C	10300 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Delrin® 127UVE NC010 Acetal Homopolymer (Unverified Data**) Delrin® 127UVE NC010 (formerly DE20555) is a high viscosity acetal homopolymer with UV stabilizers having extremely low VOC emissions, developed for automotive interior applications.Information pro..
Tensile Strength, Yield	71.0 MPa @Temperature 23.0 °C	10300 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Delrin® 300CP NC010 Acetal Homopolymer (Unverified Data**) Delrin® 300CP is a medium-high viscosity acetal homopolymer with improved thermal stability and an outstanding balance of ease of processing and part performance.Information provided by DuPont Perf..
Tensile Strength, Yield	71.0 MPa @Temperature 23.0 °C	10300 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Delrin® FG500TL NC010 Acetal Homopolymer (Unverified Data**) Delrin® FG500TL medium viscosity acetal homopolymer resin containing 1.5% Teflon® PTFE Micropowder. It has been developed for consideration into applications such as parts for the food industry.In..
Tensile Strength, Yield	71.0 MPa @Temperature 23.0 °C	10300 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Delrin® FG900P NC010 Acetal Homopolymer (Unverified Data**) Delrin® FG900P is a low viscosity acetal homopolymer, with improved thermal stability. It has been developed for consideration into applications such as parts for the food industry.Information prov..
Tensile Strength, Yield	71.0 MPa @Temperature 23.0 °C	10300 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Delrin® SC690 NC010 Acetal Homopolymer (Unverified Data**) Delrin® SC690 is a low viscosity acetal homopolymer, developed for parts requiring high precision molding in the healthcare industry.Information provided by DuPont Performance Polymers
Tensile Strength, Yield	71.0 MPa	10300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RAP22 PA 66 LNP* LUBRICOMP* RAP22 is a compound based on Nylon 66 resin containing 10% Aramid, 10% PTFE/Silicone. Added feature of this grade includes: Wear Resistant.
Tensile Strength, Yield	71.0 MPa	10300 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RL004 PA 66 LNP* LUBRICOMP* RL004 is a copmpound based on Nylon 66 resin containing 20% PTFE. Added feature of this grade includes: Wear Resistant.
Tensile Strength, Yield	71.0 MPa	10300 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp AF0029 ABS LNP* Thermocomp* AF0029 is an ABS base resin containing Glass Fiber. Characteristics of this grade are Flame Retardancy.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield	71.0 MPa @Temperature -40.0 Â°C	10300 psi @Temperature -40.0 Â°F	ISO Data
Styrolution LuranÂ® S 757 G ASA Luran S 757 G is an easy flowing injection molding ASA grade with large flow path/wall thickness ratios.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Tensile Strength, Yield	71.0 MPa	10300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP 9X10401H ABS LNP* THERMOCOMP* 9X10401H is a compound based on Polyphenylsulfone containing proprietary filler(s). Added feature of this grade is: X-Ray Opaque.
Tensile Strength, Yield	71.0 MPa	10300 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL EM7301HF PPE+PS (Asia Pacific) Easy flow, 10% glass filled, improved adhesion PPO/HIPS alloy.
Tensile Strength, Yield	71.0 MPa	10300 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL EN7010 PPE+SEBS (Asia Pacific) High heat, Non halogenated flame retardant Noryl product for Film
Tensile Strength, Yield	71.0 MPa	10300 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL LTA6020 PPE+PS (Europe-Africa-Middle East)
Tensile Strength, Yield	71.0 MPa	10300 psi	SABIC - Japan Method
SABIC Innovative Plastics NORYL PX1712 PPE+HIPS (Asia Pacific) PPE/HIPS unfilled high heat for auto interior
Tensile Strength, Yield	71.0 MPa	10300 psi	ASTM D638
Washington Penn Homopolymer Polypropylene 27% Glass Reinforced Fiberglass & mineral-reinforced polypropylene compounds provide excellent tensile and impact properties. Mold shrinkage is similar to ABS and polystyrene. Compounds also have dimensional stability. ..
Tensile Strength, Yield	71.0 MPa	10300 psi	ISO 527-2
Tisan TISLAMID® 6 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec..
Tensile Strength, Yield	71.0 - 77.0 MPa	10300 - 11200 psi	Cure: 1h/80°C/140°C; ISO R 527-1966
Hexcel® HexFlow® RTM 120/HY 2954 120°C Epoxy System for RTM Two Component System RTM 120/HY2954 is a two component system, developed for the manufacture of high performance Aerospace and Industrial composite parts using the Advanced Resin Transfer Moulding Process.
Tensile Strength, Yield	71.0 MPa	10300 psi	ISO 527-1/-2
DuPont Performance Polymers Delrin® 100P NC010 Acetal (POM) (Unverified Data**) High Viscosity Acetal Homopolymer with Improved Processing Delrin 100P is a high viscosity acetal homopolymer for use in easy to fill molds. It has improved processing thermal stability good mechani..
Tensile Strength, Yield	71.0 MPa	10300 psi	ISO 527-1/-2
DuPont Performance Polymers Delrin® 127UVE NC010 Acetal (POM) (Unverified Data**) UV Stabilized High Viscosity Acetal Homopolymer with Very Low Emissions Delrin 127UVE NC010 (formerly DE20555) is a high viscosity acetal homopolymer with UV stabilizers with very low VOC emissions ..
Tensile Strength, Yield	71.0 MPa	10300 psi	ISO 527-1/-2
DuPont Performance Polymers Delrin® 300CP NC010 Acetal (POM) (Unverified Data**) Medium-high Viscosity Acetal Homopolymer with Improved ProcessingDelrin 300CP is a medium-high viscosity acetal homopolymer with improved thermal stability and an outstanding balance of ease of proc..
Tensile Strength, Yield	71.0 MPa	10300 psi	ISO 527-1/-2
DuPont Performance Polymers Delrin® 327UVE NC010 Acetal (POM) (Unverified Data**) UV Stabilized Medium-high Viscosity Acetal Homopolymer with Very Low Emissions Delrin 327UVE NC010 (formerly DE20554) is a medium-high viscosity acetal homopolymer with UV stabilizers with very low ..
Tensile Strength, Yield	71.0 MPa	10300 psi	ISO 527-1/-2
DuPont Performance Polymers Delrin® 500P BK602 Acetal (POM) (Unverified Data**) Medium Viscosity Acetal Homopolymer with Improved ProcessingDelrin 500P BK602 is a general purpose medium viscosity black acetal homopolymer resin for injection molding. Delrin 500P has improved pro..
Tensile Strength, Yield	71.0 MPa	10300 psi	ISO 527-1/-2
DuPont Performance Polymers Delrin® PC690 NC010 Acetal (POM) (Unverified Data**) Low Viscosity Acetal Homopolymer Developed for the Healthcare Industry Delrin SC690 is a low viscosity acetal homopolymer developed for parts requiring high precision molding in the healthcare indus..
Tensile Strength, Yield	71.0 MPa	10300 psi	ASTM D638
Aclo Accutech ABS ABS831G20L Glass Reinforced
Tensile Strength, Yield	71.0 MPa @Temperature 23.0 °C	10300 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Delrin® 300CP BK642 Acetal Homopolymer (Unverified Data**) Delrin® 300CP is a medium-high viscosity acetal homopolymer with improved thermal stability and an outstanding balance of ease of processing and part performance. This black is formulated to mainta..
Tensile Strength, Yield	71.0 MPa	10300 psi	10%/min. ASTM D638
EVALCA EVAL® LC-T101 Ethylene Vinyl Alcohol Copolymer Resin (discontinued **) 32 mol % Ethylene.Data provided by EVALCA. Applications: Solid phase pressure forming. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produc..