SABIC Innovative Plastics LNP LUBRICOMP RAP22 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RAP22 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RAP22 is a compound based on Nylon 66 resin containing 10% Aramid, 10% PTFE/Silicone. Added feature of this grade includes: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.710 % | 0.710 % | 50% RH, 24 hrs; ASTM D570 |
| 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
| 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
| 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| 5.9 % | 5.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.39 GPa | 492 ksi | 50 mm/min; ASTM D638 |
| 3.42 GPa | 496 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| Flexural Modulus | 3.25 GPa | 471 ksi | 2 mm/min; ISO 178 |
| 3.26 GPa | 473 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.42 J/cm | 6.41 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.37 | 0.37 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.26 | 0.26 | ASTM D3702 Modified |
| K (wear) Factor | 46.3 x 10-8 mm³/N-M | 23.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 49.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
48.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 224 °C | 435 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 189 °C @Thickness 3.20 mm |
372 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Raschig Group EN 5007 Epoxy Molding Compound
- Garlock 50 Natural/SBR Sheet Rubber
- Kinlead LSD11 Low Temperature Grade Heat Sealable Film (thickness: 18 µm)
- LyondellBasell Astryn BB73F Polypropylene Copolymer, Mineral Filled
- ExxonMobil CM-P Mobilgrease CM Series
- UBE UBESTA® 3030JNU Short Cycle Time Electronic Grade Nylon 12
- CoorsTek YZTP Yttria Partially Stabilized Zirconia, Hipped
- Diamond Polymers ABS 9501
- Arlon 51943C014 0.014" (0.356 mm) Cured Silicone Rubber with Fiberglass Substrate
- BorsodChem ONGROVIL S-5067 Suspension PVC-Resin
Copyright © lookpolymers.com All Rights Reserved